2010012580 生材1002班 张成彬 聚乙二醇生物降解.pdf

聚乙二醇生物降解 张成彬 (北京化工大学材料科学与工程学院，北京市朝阳区，10029) 摘要:聚乙二醇具有良好的生物相容性和两亲性,在生物医药领域中有着广泛 的应用。本文对聚乙二醇的生产、应用以及对生物降解研究进行详细的评述。 聚乙二醇的降解性能取决于分子量的大小,分子量较高的降解不佳。聚乙二醇的 好氧代谢作用机理已较清楚:首先被氧化成乙醛和一元羧酸,进一步进行解聚; 但其厌氧代谢作用机理尚不明确,已提出的许多机理还有待进一步研究确证。 关键词：聚乙二醇；生物降解；生产；合成 BIODEGRADATION OF POLYETHYLENE GLYCOLS ZHANG Cheng Bin(College of Materials Science and Engineering Beijing University of Chemical Technology，Chaoyang Beijing 100029) Abstract : Polyethylene glycol has good biocompatibility and amphiphilic, has a wide range of applications in the biomedical field .Preparation 、application 、biodegradation of polyethylene glycols(PEG) is reviewed in this paper .The degradability of PEGs depends on the molecular weight .Higher molecular weight results in poor degradation .Aerobic metabolism of PEGs are clear: first oxidized to an aldehyde and monocarboxylic acid , then followed by depolymerization .On the other hand ,the mechanism of anaerobic metabolism is still not clear, most of the proposed mechanisms need to be firmed . Keywords: Polyethylene glycol, biodegradation, preparation, application 1.前言 1 聚乙二醇(PEG)由环氧乙烷开环聚合得到，根据生产工艺路线的不同，也 有文献称作聚氧化乙烯(PEO)【1】。1940 年由美国陶氏(DOW)公司商业化生产， 因其具备优良的保湿性、润滑性、分散和黏结性，被广泛应用于食品、医药、 护理用品、化工等行业。随着材料科学技术的发展，要求高分子材料应同时 具备多方面的优良性能。单一高分子材料很难满足这一要求，因此通过对已 有高分子材料的共混改性而设计和制备所需的材料越来越受到材料科学家的 【2-3】 青睐 。 聚乙二醇是一类特殊的聚合物，作为原材料用于合成洗涤剂和聚氨酯已 有很长的历史。它们或是水溶的，或是油状液体，并发现它们最终进入了环 境或污水系统。对于进入这些水域的材料，由于它们既不能循环利用又不能 焚烧，因此它们就必须具有生物可降解性。 本文综述将描述聚乙二醇聚合物的合成、应用，然后将详细讨论PEG 的生物降解，最后将介绍一下当今的生产现状与市场分析。 2.历史概况 PEG 最初是在 Carbowax 商标名下商业生产的，它的数均分子质量(M)为 200 ～2000Da 。在 20 世纪 50 年代，已有可能合成更大的聚环氧己烷 (polyethylene oxide，缩写作 PEO)，其范围为几十万至几百万道尔顿。大部