600MW 超临界机组循环水泵振动大的原因分析及 - 中国大唐集团公司.PDF

2014 论文汇编 600MW 超临界机组循环水泵振动大的原因分析及处理 赵晓飞 ，李永俊，董少平 （广东大唐国际潮州发电有限责任公司 ） 摘 要：针对潮州发电公司某台循环水泵检修后短期内振动幅值快速上升的情况，从海水电 化学腐蚀机理着手，分析认为主要原因是缝隙腐蚀、电偶腐蚀、外加阴极保护电流缺失等加 剧镍铬铸铁材质外筒体定位面的腐蚀速率，引起泵体可抽出部件与外筒体定位面之间配合间 隙严重超标并出现偏斜，导致水泵导轴承失去支撑定位作用且动静部件不同心造成的。通过 修复阴极电流保护系统，有选择性的提高外筒体局部材质等级，循环水泵振动大问题已得到 解决。 关键词：循环水泵；海水腐蚀；缝隙腐蚀；电偶腐蚀；防腐蚀措施 [Abstract] According to the Chaozhou power company of a circulating pump maintenance shortly after the rapid rise of the vibration amplitude, starting from the mechanism of electrochemical corrosion of seawater, analyses that the main reason is the crevice corrosion, galvanic corrosion, cathodic protection and lack of cast iron cylinder positioning surface increased the corrosion rate, the withdrawable part between pump body to deflect, and the cylinder the positioning surface clearance of serious exceed the standard, the static and dynamic components are not concentric, resulting in water pump guide bearing lost support from. Through the repair of impressed current cathodic protection system, improve the grade of the material cylinder local selective, circulating water pump vibration problem has been resolved. [Keywords] circulating water pump; seawater corrosion; crevice corrosion; galvanic corrosion; corrosion protection measures 1 引言 循环水泵是现代大型火力发电厂的重要辅机，其主要作用是向凝汽器提供大流量、 低扬程的冷却水，冷凝汽轮机低压缸排汽，使凝汽器形成高度真空；同时也向闭式水 热交换器供应冷却水。 由于海水对钢铁具有强腐蚀性，以及外加阴极电流保护系统维护检修不到位，沿 海电厂循环水泵部件腐蚀问题日益突出，并引发水泵部件损坏、振动增大、甚至被迫 停运等后果，严重影响机组的安全经济运行 。本文就潮州发电公司某台循环水泵检修 后短期内振动快速增大情况作以介绍和分析。 864 2014 论文汇编