影响铁水脱硫过程粘渣物形成的因素分析.pdf

热能工程 《工业加热》第37 卷2008 年第4 期 影响铁水脱硫过程粘渣物形成的因素分析 欧阳德刚，罗安智，王清方，李具中 （武汉钢铁集团公司研究院，湖北 武汉 430080） 摘要：根据不同脱硫工艺条件下粘渣物成分的检验结果，探讨了熔渣的成分与性能、粘渣面工作温度与工作状况、脱硫工艺等因 素对粘渣物形成的影响关系，分析了脱硫器具与脱硫铁水罐粘渣的危害，探明了铁水罐粘渣物清除困难的主要原因，指出了喷吹 脱硫过程中熔渣与铁水喷溅对粘渣物铆钉状结合的促进作用。 关键词：粘渣物；成分；铁水脱硫工艺；脱硫铁水罐；脱硫器具 ( ) 中图分类号：TF74 1.344 文献标志码：A 文章编号：1002- 1639 2008 04-0004-04 Analysis of Factors on Forming Slag in The Liquid Iron Desulphurization Process OUYANG De-gang, LUO An-zhi, WANG Qing-fang, LI Ju-zhong (Wuhan Iron Steel Group Corp.reserch institate, China) Abstract ：The composition of felting slag was examined. The influencing relations of the factors of composition and perfomance of felting slag, status and temperature of surface felting slag, desulphurizing technics etc on forming slag were discussed. The harm of slag felting on the desulphurization apparatus and liquid iron tin were analyzed. The main causes to eliminate slag felting on liquid iron difficultly were proved up . The promoting action of slag and liquid iron splashing during inj ection dusulphurization on felting slag rivelt combination was pointed out. Key words ：slag ；compositon ；liquid iron desulphurizing technics ；liquid iron desulphurization tin ；desulphurization apparatus 粘渣是钢铁冶金行业常见的一种现象，主要出现在 分析可见，粘渣物中铁含量较高，粘渣物沿着铁水罐上 与熔融金属紧密接触的器壁表面1 1 。对于铁水脱硫系统， 部自由空间的罐壁与罐沿形成完整的结圈，具体如表1 和 粘渣主要表现为脱硫器具壁面、盛铁容器内壁面、防溅 图1、图2 所示。 罩内表面等部位，其中，脱硫器具壁面的粘渣将导致脱 表 1 粘渣物化学成分 % 硫器具使用性能的下降，甚至导致使用性能的丧失；脱 品名 （ ） （ ） （ ） （ ） （ ） SiO Al O CaO MgO TFe