T i2IF , , , , (山东大学 材料科学与工程学院, 山东 济南 250061) : Ti2IF钢经铁素体区热轧、退火后, 用电子探针和扫描电镜研究了析出物的尺寸、形 、分布等特征和析出方式。 讨论了析出物的析出机制和脱氧产物对析出物的影响。结果表明, 铁素体区轧制与传统轧制方式的析出物相同; 析 出物多在晶内析出, 少量在晶界上析出, 析出方式以单独析出为主, 存在TNi 2TiC和TNi 2Al O 的复合析出。 2 3 : Ti2IF钢; 析出物; 电子探针; 析出机制 : TG 142. 4; TG 113. 1 : A : 025426051(2006) 0120079204 Study on the P re ip itates of T i2IF SteelH ot2Rolled in Ferr ite R egion JING Cai2nian, WANG Zuo2chen , HAN Fu2tao, YIYan2hon , ZHANG Wen2p in ( School ofMater ials Science and En ineerin , Shandon Un iversity, Jicnan Shandon 250061, Ch ina) Abstr a t: Ti2IF steelwas hot2rolled in the ferrite re ion and annealed, the precip itates characteristic such as size, mor2 pholo y, distribution was analyzed by electron probem icroanalysis ( EPMA) and scannin electron m icroscopy ( SEM ). The precip itation mechanism and the effect of deoxidation production on precipitates were discussed. The resu lts show that the precipitates characteristic of ferrite2rolledTi2IF steels is sam e as the traditional technolo y, most of the precipi2 tates are appeared in the rain inner, a few are appeared on the rain boundary, some TNi 2TiC and TNi 2Al O are com2 2 3 plex precipitation. K ey w ord s: Ti2interstitial2free stee;l precip itate; electron probe m icroanalysis (EPMA); precip itation mechanism 1 引言 验在四辊试验轧机上进行, 先将板坯加热到 1000e , IF钢是在超低碳钢( 01005wt% C)中添加Ti、Nb 保温 1h, 然后空冷至 800e , 按设定的工艺参数轧至 等强碳、氮化合物形成元素, 与钢中的 C、N 原子反应 3mm, 总压下量为 88%, 轧制时使用了润滑油。热轧 生成碳、氮化合物, 基体呈无间隙原子状态。由于不含 后的钢板空冷至室温, 然后装入带保护气氛的退火炉 间隙原子, IF钢具有高的塑性各向异性 ( r)值、高的加