重晶石矿粉表面改性研究与应用-南京能德化工有限公司.PDF

2005年第6期 中国非金属矿工业导刊 总第51期 [试验研究] 重晶石矿粉表面改性研究与应用 1 2 王 威，欧阳兆辉 （1.武汉亚东水泥有限公司，湖北 武汉 430081；2.武汉科技大学应用化学研究所，湖北 武汉 430081） 摘要：利用硬脂酸、硅烷偶联剂对重晶石粉进行表面改性。改性后的重晶石矿物表面的疏水性得到明显了改善；分析了 改性时间、改性温度和改性剂用量等因素对改性效果的影响。应用实验表明：改性超细粉在铜版纸涂布和油漆中可以替代沉 淀硫酸钡。 关键词：重晶石矿粉；表面改性；硅烷偶联剂；硬脂酸 中图分类号：TD975.1;TD985 文献标识码：文章编号： A Study and Application on Surface Modification of Barite Powder 1 2 Wang Wei , Ouyang Zhaohui (1.Wuhan Yadong Cement Limited Liability Company, Wuhan, Hubei, 430081 ; 2.Research Institute of Applied Chemistry, Wuhan University of Science and Technology, Wuhan, Hubei, 430081) Abstract: Barite powder was modified with stearic acid and silicane. The activity index indicated that modified barite powder had a good hydrophobic. The effect of modification was discussed separately through the processing time, processing temperature and quantity of reagents. Application experimentation show that modified barite powder takes the place of precipitated barium sulfate in offset coated paper, coating and paint etc. Key words: barite powder; surface modification; silicane; stearic acid 1 前言 学组成为：BaSO94.36%，FeO含量0.274%，其他 4 2 3 3 重晶石是一类重要的含钡矿物，具有密度大、 5.366%；密度为4.0～；白度为4.5g/cm87.20%。 [1] 实验用的改性剂：硬脂酸和WD-60[-(2，γ3- 化学性质稳定的特点，应用于许多工业部门 。重晶 石是我国的优势矿产，我国重晶石探明储量已达 环氧丙氧)丙基三甲氧基硅烷]；溶剂有无水乙醇、异 3.64，全国重晶石矿建成规模达亿t 420万t。目前，丙醇。 我国工业上利用的重晶石，主要是初级产品，即破 2.2实验方法　 碎成200目和325目后用作填料。由于无机矿物与有 硬脂酸改性重晶石超