多孔膨胀珍珠岩轻集料混凝土分层离析控制技术研究.pdfVIP

多孔膨胀珍珠岩轻集料混凝土分层离析控制技术的研究 杨 萍，赵维霞，杨进超，蔡溪南，袁晓宁，樊晓苓 （西北核技术研究所，西安710024） 摘要：探讨了多孔膨胀珍珠岩轻集料混凝土分层离析产生的原因，采用掺入适量粉煤灰、高效外加剂并对多孔膨胀珍珠 岩进行预湿处理等技术措施有效防止了轻集料混凝土的分层离析，配制出了具有优良工作性和匀质性，不离析、低收缩， 易于浇注和开挖的CL5～CL10多孔膨胀珍珠岩低强轻集料混凝土。 关键词：多孔膨胀珍珠岩；低强；轻集料混凝土；离析；控制技术 Studyoncontroltechnologyofsegregationofporousexpandedperlitelightweight aggregateconcrete YANGPing,ZHAOWei-xia,YANGJin-chao,CAIXi-nan,YUANGXiao-lin,FANXiao-lin (NorthestResearchInstituteofNuclearTechnolgy，Xi′an710024，China) Abstract: The article discusses about the reason of segregation of porous expanded perlite lightweight aggregate concrete, the segregation problem of the lightweight concrete has been resolved successfully by adding fly ash, high performance admixture and porous expansive perlite pre-wetting and other technical measures, the porous expanded perlite lightweight concrete CL5-CL10 was prepared with good workability anduniformity,nosegregation,easeofcastingandexcavation. Keywords:porousexpandedperlite;light-weightaggregateconcrete;segregation;controltechnology 前 多孔膨胀珍珠岩轻集料混凝土具有轻质、保温、隔音、利于开挖等性能。轻集料分层离析现象一直 是轻集料混凝土领域内公认的难题之一，轻集料的分层离析导致混凝土匀质性变差、硬化混凝土性能劣 化，从而影响轻骨料混凝土推广应用，国内外都十分关注这一问题目前，为此，开展控制多孔膨胀珍珠 岩轻集料混凝土分层离析技术的研究十分必要。本文针对轻集料混凝土易分层离析这一问题，对其影响 因素进行了分析，采用水泥为胶凝材料，粉煤灰的填料，膨胀珍珠岩为集料，适量的外加剂以改善浆体 的性能对轻集料混凝土分层离析程度进行了研究。 1 分层离析原因 1.1 组分间密度差异 离析可以定义为新拌混凝土的各个组分发生分离并使其分布不均匀的一种特性。泌水是在较重(轻) 的固体组分沉降(上浮)时，组成材料的保水能力不足以使拌和水处于分散状态所引起的，所以泌水是离 析的一种形式。多孔膨胀珍珠岩低强轻集料混凝土易出现泌水、分 、离析的主要原因在于原料级配不 合理及组分间的密度差异，导致各组分发生相对运动(上浮或下沉)，而这种运动在外力作用下会加速， 从而引起密度较小的多孔膨胀珍珠岩和水的上浮，密度大的水泥等下沉，造成各组分分离或富集一处， 从而导致拌合物不均匀和失去连续性的现象，进而导致混凝土整体的不均匀，最终导致了混凝土的分 离析。同时，由于密度较小的水在上浮的过程中，一部分会遇到相对较大的多孔膨胀珍珠岩并受其阻止， 在多孔膨胀珍珠岩下面形成一个水囊；另一部分不受阻碍会一直上浮至拌和物的表 ，在其蒸发后则形 成空穴，是轻集料混凝土最薄弱的环节，也是轻集料混凝土渗水的主要通道和裂缝的发源地。如图１为 轻骨料混凝土拌和物分层结构的形成过程。 图1 拌和物分层结构形成过程 1.2 较严重的泌水 一般来说，混凝土拌和物从制备、浇筑到凝结的全过程，可以说几乎没有不泌水的混凝土，混凝土 少量泌水是一种正常的现象，但泌水现象太严