大型渗碳淬火齿圈预处理工艺探讨.pdfVIP

第29卷第1期 热处理技术与装备 Vo1．29．No．1 2008年2月 RECHULI JISHU YU ZHUANGBEI Feb．2008 · 工 艺 · 大型渗碳淬火齿圈预处理工艺探讨 邢大志 (重庆齿轮箱有限责任公司，重庆402263) 摘 要：根据热处理产生形变的普遍规律分析，正火与调质所产生的残余应力不同，其产生形变的规 律也不同。对于大型渗碳淬火齿圈，预处理采用调质与正火进行比较，调质可以得到更加均匀分布 的碳化物形态，其形变规律与最终的渗碳淬火形变规律一致，更有利于减小零件的热处理畸变。 关键词：大型渗碳淬火齿圈；预处理；正火；调质 中图分类号：TB332 文献标识码： B 文章编号：1673—4971(2008)01—0057—03 Study on Pre--treatment for Large--scale Carburized Gear Rim XING Da．zhi (Chongqing Gearbox Co．，Ltd．，Chongqing 402264，China) Abstract：This paper analyses simply the distortion from the heat treatment according to general principle． It is considered that the residual stress is different as comparing the normalization and the quenching and tempering．The tendency of distortion is different too．The pre—treatment process of large—scale carbu- rized gear rim can get more uniform distribution of carbide by quenching and tempering than by normaliza- tion．Its tendency of distortion is game as the final carburization and quenching．It is more benefit to de- crease the distortion from the heat treatment． Key words：large··scale carburized gear rim；pre··treatment；normalization；quenching and tempering 0 前言 第三代重载齿轮，即渗碳淬火硬齿面齿轮。 众所周知，根据齿轮零件的服役条件，齿轮热处 我国是在上世纪8O年代才逐步引进了此项技 理的方法也有很多。但是随着现代科技的长足发展 术，我公司也正是在此时引进了德国的此项专利技 和人们对齿轮承载能力不断提出苛刻要求，使得渗 术，开我国大型低速重载硬齿面齿轮之先河，并逐步 碳淬火这一传统的热处理工艺成为齿轮热处理的主 取代了进口大型硬齿面齿轮箱。 流，据有不可替代的地位。如上世纪5O年代的大型 大型硬齿面齿轮的出现，展示了其无比的优越 低速重载齿轮，大多是采用正火或调质的软齿面齿 性，是其它热处理方法不可企及的。但因其发展时 轮，直到5O年代末发展了中硬齿面齿轮，把齿面硬