自收缩测试方法及试验研究.pdfVIP

混凝土自收缩测试方法与试验研究 朱耀台 （浙江大学建筑工程学院 浙江 杭州 310027 ） 摘要：自收缩是造成目前混凝土工程中早期裂缝的主要原因，然而对于混凝土自收缩目前还 没有形成统一的测试方法。本文主要介绍了国内外学者提出的用于混凝土早期自收缩的测试 方法，结合自行设计的测试方法及试验结果对测试当中存在的一些问题做了分析，以期对相 关研究人员提供借鉴。 关键词：早期开裂； 自收缩； 测试方法； 泌水 Test Methods and Experimental Study on Autogenous Shrinkage of Concrete Zhu Yao-tai (Building engineering college of Zhejiang University, Hangzhou, 310027, China) Abstract: Autogenous shrinkage is the main reason for the early age cracking of concrete engineering, however the unitized test method has still not been formed by now. In this paper, various test methods for autogenous shrinkage measurement put forward by the researchers at home and abroad have been introduced. Combining with the test method designed by self and the test results achieved, some problems occurred during the tests have also been analysed. It is expected that the researchers correlated will borrow ideas from the paper. Key words: early age cracking; autogenous shrinkage; test methods; bleeding 1 概述 混凝土的自收缩是指混凝土在没有与周围环境发生湿度交换的情况下发生的体积变 化，它是水泥水化过程中由于没有外界水供应或外界水通过毛细孔迁移到体系内部的速度小 于水化耗水速度时引起的混凝土内部的自干燥[1] [2]过程导致，自干燥对于自收缩的作用机理 与干燥收缩类似。这一现象在上世纪三四十年代就由 Lyman[3] [4] 、Davis 等人先后发现。然而 由于当时的混凝土水灰比大，又没掺任何矿物细掺料等诸多原因，所以自收缩的量很小， Davis 测得的自收缩在 50～100×10-6 之间，比干燥收缩小了一个数量级，考虑到一般测得 的干燥收缩包含了自收缩，因此那以后相当长的时间里自收缩被忽略了。随着高强高性能混 凝土技术在上世纪 80 年代早期发展并得到了推广应用以来，自收缩问题又从新引起了人们 的注意。Paillere 等人[5]发现低水胶比的高性能混凝土在约束作用下密封养护时，自收缩会 引起贯通裂缝的产生；Holland 等人[6]在实际施工过程中也发现，大坝消能池修复所用的超 高强混凝土在施工后 2～3d 内产生了贯通裂缝；Wittmann [7] [8] 以及国内的安明喆等 都认为自 收缩是引起混凝土早期开裂的主要原因。进入 90 年代以来早期开裂问题越来越严重，很多 现浇梁板拆模时甚至在浇筑后的 6 至 12 小时内就出现了裂缝。因此研究混