502胶水配方（502 glue formula）.docVIP

502胶水配方（502 glue formula） The formulation of 1] ethylene vinyl acetate copolymer 100 coumarone indene resin 25 synthetic resin 7 paraffin talc powder 202 6- butylated hydroxytoluene 1 this formula for general varieties, the softening temperature of 72-80 DEG C, brittle temperature at -40 DEG C, can be used for a long time in the -40 - 60 degrees C. All kinds of materials have better adhesive properties, especially for some difficult to adhere to plastic. [formula 2] ethylene vinyl acetate copolymer 100 butyl rubber 30 butyl phenol resin 20 The matrix dibutyl phthalate 5 calcium carbonate 5 this formula is the vinyl acetate content of 28% low molecular weight ethylene vinyl acetate copolymer, adding butyl rubber glue to improve flexibility and elasticity, improve the adhesive strength, shorten the curing time. [formula 3] vinyl pyrrolidone vinyl acetate copolymer 100 castor oil hydrogenation compound 4 water soluble polyethylene glycol 1.62 6- wax 2.5 epoxy resin, butylated hydroxytoluene 1.4 this formula is a water-soluble hot-melt adhesive. The matrix is an ethylene vinyl acetate copolymer modified by pyrrolidone. Higher molecular weight and higher bonding strength. The solubility of the wax compounds is poor, and water-soluble polyethylene glycol wax is added, which greatly improves the phase solubility. Mainly used in wood, ceramics, concrete components, fabrics, paper and other porous materials bonding, can also be used as other adhesives bottom adhesive. [formula 4] ethylene vinyl acetate copolymer 100, rosin 75, barium sulfate 75, antioxidant 1.25 In the formula, the substrate is ethylene vinyl acetate copolymer with a melting index of 24 and a vinyl acetate content of 32%. It is mainly used for edge sealing of wood-based panels in wood industry. [formula 5] ethylene vinyl acetate copolymer 100 paraffin 20 polymerized rosin (softening point 120 degrees C) 30 N- phenyl -?? 1 - naphthylamine this formula of matrix of vinyl acetate content of more than 28%. It ca