qpq热处理定义及特点（Definition and characteristics of QPQ heat treatment）.doc

qpq热处理定义及特点（Definition and characteristics of QPQ heat treatment） QPQ process (liquid nitriding) QPQ salt bath composite treatment is an advanced technology for surface modification of metal fused salt. The workpiece in two kinds of different properties of molten salt liquid successively in the processing, make a variety of elements simultaneously penetrate into the metal surface, forming a compound layer composed of several compounds, strengthens the modified metal surface, wear resistance, corrosion resistance and fatigue resistance have been improved greatly at the same time. The technology also has the advantages of energy saving, pollution-free and almost no deformation. With the advanced technology, superior performance and stable quality, it has been widely welcomed by users. It has been popularized in a large area. First, the main features: QPQ composite treatment and a single increase in wear resistance of traditional heat treatment technology and a single corrosion resistance of the table Compared to surface processing, it can: 1., the surface hardness, wear resistance, corrosion resistance and fatigue resistance of the products are greatly improved simultaneously. For example, the wear resistance of 45# steel and 40Cr steel (annealed) treated by QPQ salt bath is up to quenching and high More than 16 times of frequency quenching; 20# steel treated by QPQ salt bath has 9 times the wear resistance of carburizing and quenching It is more than 2 times hard chromium plated and ion nitrided. Fatigue limit of 45 steel treated by QPQ salt bath Increase 4O% or so. For example: 45 steel by QPQ treatment, in the atmosphere and salt fog corrosion resistance than hard chromium plating more than 16 times, than Blackening is over 7O times higher. 2. can replace a variety of processes It is often used instead of carburizing, quenching, high frequency quenching, ion nitriding, soft nitriding, quenching and tempering, etc. Quenching and other conventional heat treatment and