N44SH高性能烧结NdFeB永磁材料的开发 Development of N44SH High-Grade NdFeB Sintered Magnet Material.pdfVIP

N44SH高性能烧结NdFeB永磁材料的开发 郝忠彬，张义龙，包大新，杜君峰，谭春林，王军强 (横店集团东磁股份有限公司，浙江东阳322118) 摘要：介绍了N44SH高性能烧结NdFeB磁体的工艺技术．采用先进的双合金工艺、片铸(sC)工艺，氢 爆限D)+气流磨(JM)制粉技术，结合密封式高磁场取向成型技术和防氧化措施。先进的工艺有助于获得理想的 高综合磁性能烧结NdFeB磁体． 关键词：烧结NdFeB磁体；双合金法；片铸；磁．睦能 中图分类号：TM273 文献标识码：B ofN44SH NdFeBSinteredMaterial DevelopmentHigh—Grade Magnet HAO Zhong-bin，ZI-IANGYi-long，BAODa—xin，TANChun-lin,DUJun·feng，WANGJtm-qiang CenwalResearch DMEGC 322118,China Institute,HengdianGroup MagneticsCo,Ltd,Dongyang Abstract：Thefor N44SH NdFeB hasbeendescribedin processproducinghigh—grademagnet this群lp既Dual withthe alloyprocess，stripcasting，hydrogendecrepitation(HD)，jetmilling(JM)alongairtightmouldingtechnology andthe oxidation meas啪wereused．Advancedand attributetotheideal protection technology proper process microstructureand a have thesinteredNdFeB result,We consequentlyhighmagneticproperties．As produced magnet 谢thexcellent integratedproperties NdFeB words：sintered Key magnet；dualalloying；stripcasting；magneticproperties 1引言 近年来，NdFeB磁体所占的市场份额飞快增 介绍N44SH烧结NdFeB磁体的开发过程。 长，应用领域也在不断扩展，同时对磁体性能也提 出了更高的要求【¨。随着人们环保意识的增强，风 2实验方法 力发电机倍受关注，有人预计未来15年中国将消 耗掉3．6万吨NdFeB磁体用于风力发电机领域，扩 的Fe、含B 22％的B．Fe为主原料，用Dy、Tb取 展到全球，这个消耗量将相当惊人。风力发电机对 代部分Nd，用Co取代部分Fe。采用双合金法制 磁体的综合磁性能要求较高，要求磁体具有较高 备NdFeB合金，主合金成分设计为 ㈣一的同时凰在1