Permeabilityfrequency spectra of Nanoperm （渗透率频率光谱Nanoperm）.pdfVIP

phys. stat. sol. (a) 202, No. 3, 476–480 (2005) / DOI 10.1002/pssa.200406926 Permeability-frequency spectra of Nanoperm alloys at different temperatures *, 1 2 1 2 2 2 1 W. Qin , F. Xu , Y. J. Wu , W. L. Gao , J. C. Tang , Y. W. Du , and Y. F. Zhang 1 Research Institute for Micro/Nanometer Science and Technology and Key Laboratory for Thin Film and Microfabrication Technology of Ministry of Education, Shanghai Jiao Tong University, Shanghai 200030, People’s Republic of China 2 National Laboratory of Solid State Microstructures and Department of Physics, Nanjing University, Nanjing 210093, People’s Republic of China Received 18 June 2004, revised 26 November 2004, accepted 3 December 2004 Published online 26 January 2005 PACS 61.10.Nz, 75.50.Bb, 75.60.Ch, 81.40.Rs Permeability-frequency spectra of Nanoperm alloys were studied by using an impedance analyzer in the temperature range from 80 K to 290 K. It is shown that with decreasing temperature, the initial permeabil- ity (µ ) decreases and the relaxation frequency (f ) increases, and the temperature dependence of µ f has i 0 i 0 a minimum at 140 K. These results indicate that the temperature fall reduces the domain thickness, strengthens the domain wall pinning and enhances the eddy-current loss in high frequency ranges. Rela- tive to domain thickness and resistivity, the effects of domain wall pinning strength on µ and f are domi-