水泥基材料裂隙表面溶蚀过程-IngentaConnect.PDF

See discussions, stats, and author profiles for this publication at: /publication/263607193 Leaching Behavior of Fracture Surfaces of Cement-Based Materials Article in uei Suan Jen Hsueh Pao/ Journal of the Chinese Ceramic Society · March 2011 CITATION READS 1 28 2 authors, including: efei Li Tsinghua University 111 PUBLICATIONS 818 CITATIONS SEE PROFILE Some of the authors of this publication are also working on these related projects: Shenzhen-Zhongshan Sea link project, service life design and analysis for prefabricated concrete slab View project All content following this page was uploaded by efei Li on 09 January 2015. The user has requested enhancement of the downloaded file. · 525 · 硅 酸 盐 学 报 2011 年 第39 卷第3 期 硅 酸 盐 学 报 Vol. 39 ，No. 3 2 0 1 1 年 3 月 JOURNAL OF THE CHINESE CERAMIC SOCIETY March ，2011 水泥基材料裂隙表面溶蚀过程 王晓梅，李克非 (教育部土木工程安全与耐久性重点实验室，清华大学土木工程系，北京 100084) 摘 要：研究了水泥基材料真实裂隙表面在水流动过程中开裂表面的溶蚀特性，建立了裂隙表面在水流作用下的钙离子迁移和表面溶蚀速率模型。利 用浸泡法和裂隙渗流装置对裂隙试件进行静态和动态溶蚀行为的试验研究，根据试验结果和理论模型回归了描述静态和动态溶蚀速率，并针对裂隙表 面进行了溶蚀前后的粗糙度分析。结果表明：裂隙表面在流动水作用下的溶蚀速率显著大于静水中的溶蚀速率；水流对净浆表面和砂浆表面的溶蚀速 率的影响不同；表面溶蚀过程减小了净浆表面的粗糙度但加大了砂浆表面的粗糙度。 关键词：水泥基材料；裂隙表面；静态溶蚀；动态溶蚀；粗糙度 中图分类号：O482.3 文献标志码：A 文章编号：0454–5648(2011)03–0525–06 Leaching Behavior of Fracture Surfaces of Cement-Based Materials WANG Xiaomei，LI Kefei (Key Laboratory of Safety and Durability of Civil Engineering of China Education Ministry, Department of Civil