西龙池定子铁损试验方法和步骤.docVIP

西龙池定子铁损试验方法与步骤 郑元吉1 王大勇2 王效安3 张建华4 （中国水利水电第三工程有限公司） 【摘要】：定子铁损试验是检验定子铁芯装配质量的重要手段，也是检验铁芯自身绝缘性能的重要工序，其基本方法是在定子铁芯上缠绕若干个励磁绕组，将交流电流通入绕组内，此电流在定子铁芯中产生磁场，同时产生涡流和磁滞损耗，使铁芯发热，测量铁芯总的有功损耗与温度，计算出单位重量铁芯损耗与温升，从而判别铁芯叠装的质量。 【关键词】：定子铁损 励磁电压 励磁电流 磁通密度 Xilongchi Stator Iron Loss Test methods and procedures ZHENG Yuan-ji1,WANG Da-yong2,WANG Xiao-an3,ZHANG Jian-hua4 (Sinohydro Engineering Bureau 3 Co.; Ltd.;) abstract :Stator Iron Loss Test is an important means to test the quality of the stator core assembly and the important processes of stator core to test self-insulation properties.The basic approach is wound around the stator core of a number of field winding,then flow alternating current into the winding,the current will generated the magnetic field in the stator core and also generated eddy current and hysteresis loss,making the stator core fever.Measuring the total power loss and the core temperature, then calculate the core loss and temperature per unit weight,that discriminant the quality of the stacked iron core. key words: Stator Iron Loss Excitation voltage Excitation current Magnetic flux density 1 前言 定子铁损试验是检验定子铁芯装配质量的重要手段，也是检验铁芯自身绝缘性能的重要工序，其基本方法是在定子铁芯上缠绕若干个励磁绕组，将交流电流通入绕组内，此电流在定子铁芯中产生磁场，同时产生涡流和磁滞损耗，使铁芯发热，测量铁芯总的有功损耗与温度，计算出单位重量铁芯损耗与温升，从而判别铁芯叠装的质量。如果铁芯绝缘不好或铁芯装配质量不佳，当铁芯通过交变磁通时，涡流损耗就会增加，造成局部过热，加速铁芯绝缘和线棒绝缘老化，严重时将造成铁芯绝缘烧伤或线棒击穿事故。因此大型水轮发电机定子在现场叠装后，定子铁芯必须进行铁损试验，通过测定温升及单位铁损的方法检查叠片质量。 2 发电机相关数据 　 发电机 电动机 发电机型号 SPEL.IEC/60034-1 额定容量 333300KVA 319600KW 额定电压 18KV 18KV 额定电流 10691A 10662A 额定功率因数 0.9（滞后） 0.975（超前） 额定转速 500r/min 500r/min 额定频率 50HZ 50HZ 额定励磁电流 2010A 1780A 额定励磁电压 262V 262V 表1 3 试验标准 根据国标规定以及厂家铁损试验守则，铁损试验采用0.8-1.0特拉斯的磁通密度，持续时间为90分钟。试验合格标准：实测单位铁损不大于1.495w/kg，铁芯最高温升不超过25℃，铁心相互间最大温差不超过15℃。 4 试验接线及有关参数计算 4.1 试验接线 4.2 试验参数的计算 (1) 定子铁芯有效长度：L=K（L1-nb） 定子铁芯扼部高度：h=-ha 定子铁芯轭部截面积：S=L×h 式中 K——定子铁芯填充系数，