Corrosion Behavior of Al alloys 6061T6 Shot （铝镁合金的腐蚀行为6061 t6拍摄）.pdfVIP

ISSN: 2277-3754 ISO 9001:2008 Certified International Journal of Engineering and Innovative Technology (IJEIT) Volume 4, Issue 8, February 2015 Corrosion Behavior of Al alloys 6061-T6 Shot Peening in Different Aqueous Solution Kharia Salman Hassan, Abbas Sheyaa Alwan, Sawsan Abdulshaheed Abbas points leading to the formation of pits on the aluminum Abstract— This work are studying the effects of shot peening surface. time on corrosion behaviors of AA 6061-T6 in aqueous solutions. Corrosion of aluminum alloy takes place when it is exposed Many specimens prepared for Corrosion test with the dimensions to the presence of electrolyte having pH between 4.5 to 8.5 of (15*15*3) mm according to ASTM G71-31. The shot peening process using steel ball have diameter 2.75 mm and shot peening [3]. All mechanical surfaces treatments lead to a characteristic time at (15, 30, 45) min. The series of experimental techniques surface roughness increased near surface dislocation density have been conducted to evaluate shot peen properties of the alloys (cold work) and development of microscopic residual by carrying out hardness, surface residual stresses, microstructure stresses. Shot peened surfaces are compressive residual and surface roughness. Corrosion test by tafel extrapolation stresses and extremely high dislocation densities in near method was carried out on shot and un shot corrosion specimens