浅议现浇楼面裂缝产生原因及控制措施.doc

浅议现浇楼面裂缝产生原因及控制措施摘要：自90年代初建筑行业逐步淘汰装配式楼板结构以来，现浇钢筋混凝土楼板逐步取代了预制钢筋混凝土楼板。随之而来出现的现浇钢筋混凝土楼板的裂缝，特别是住宅工程楼板的裂缝发生后，往往会引起小业主的投诉以及索赔要求等，自2008年广州地区实行分户验收制度以来，尤其住宅楼在施工质量方面施工单位将面临的更大挑战与压力。因此控制施工过程中了出现的裂缝显得尤为重要，下面就楼面混凝土裂缝产生原因和防治措施进行分析。 关键词：现浇楼面, 裂缝 ,混凝土, 预防措施 Abstract: since the beginning of the 90 s phased out fabricated floor construction industry since the structure, cast-in-place reinforced concrete floor is gradually replacing the precast reinforced concrete floor. There followed the cast-in-place reinforced concrete floor cracks, especially residential project after the occurrence of the floor cracks, often can cause the complaints and small business owners claim, since the 2008 guangzhou region since acceptance system of the individual, especially residential buildings in the construction quality aspects of the construction unit will face more big challenge and pressure. So the process control in the construction of cracks is particularly important, below floor concrete crack causes and prevention and control measures are analyzed. Keywords: cast-in-situ floor, cracks, concrete, the preventive measures 中图分类号：TU528文献标识码：A 文章编号： 1、工程概况 本项目位于广州南沙区，框架剪力墙结构，楼板混凝土C30，厚120mm。主要由12栋塔楼组成（其中地下1层连体地下室，局部负二层人防结构），Z-1、Z-2、Z-3、Z-5栋地上33层，Z-4、Z-8栋地上29层，Z-6、Z-11栋地上28层， Z-9、Z-10栋地上26层，Z-12栋地上24层，Z-7栋地上20层，及一栋社区服务中心，一栋幼儿园组成。 2、现浇混凝土板裂缝的成因及预防措施 现就混凝土楼板面出现的裂缝进行原因分析，一般情况下，楼屋面裂缝表现为：表面龟裂，纵向裂缝、横向裂缝以及斜向裂缝。分析其原因主要有原材料及施工等方面的原因，以下将逐一具体分析。 2.1、原材料方面的原因 2.1.1水泥的水泥安定性不稳定，水泥中含有生石灰或氧化镁，这些成分在和水化合后产生体积膨胀，产生裂缝。裂缝主要表现为表面龟裂、干缩裂缝等。水泥浆中水分的蒸发会产生干缩，混凝土在凝固过程中80%的水分要蒸发，20%的水分是水泥硬化所必需的，而最初失去的30%的自由水分几乎不引起干缩变形，随着混凝土的陆续干燥而使20%的吸附水逸出，就会出现干缩裂缝。而表面干燥快而中心干燥慢，因而在表面产生拉应力而出现裂缝。混凝土干缩主要和混凝土的水灰比、水泥的成分、水泥的用量、集料的性质和用量、外加剂的用量等有关。 主要预防措施：一是选用水化热小收缩量较小的水泥，如矿渣水泥、粉煤灰水泥等，水泥应采用425号以上矿渣硅酸盐水泥或普通硅酸盐水泥。二是混凝土的干缩受水灰比的影响较大，水灰比越大，干缩越大，因此在混凝土配合比设计中应尽量控制好水灰比的选用，同时掺加合适的减水剂，在运输及施工过程中严禁加水。三是严格控制混凝土搅拌和施工中的配合比，根据实验中心给出的混凝土强度等级配合比单，在实际作业中每班应至少测两次砂石的含水量，及时调整配合比。四是加强混凝土的早期养护，并适当延长混凝土的养护时间。五是混凝土中的掺合料宜采用粉煤灰，其掺量应通过试验确定，并应符合有关