几种零件的热处理实例（Examples of several parts of heat treatment）.doc

下载文档 降价啦

6
0
约3万字
约 35页
2017-08-17 发布于河南
举报
版权申诉
保障服务

几种零件的热处理实例（Examples of several parts of heat treatment）.doc

1、本文档共35页，可阅读全部内容。
2、原创力文档（book118）网站文档一经付费（服务费），不意味着购买了该文档的版权，仅供个人/单位学习、研究之用，不得用于商业用途，未经授权，严禁复制、发行、汇编、翻译或者网络传播等，侵权必究。
3、本站所有内容均由合作方或网友上传，本站不对文档的完整性、权威性及其观点立场正确性做任何保证或承诺！文档内容仅供研究参考，付费前请自行鉴别。如您付费，意味着您自己接受本站规则且自行承担风险，本站不退款、不进行额外附加服务；查看《如何避免下载的几个坑》。如果您已付费下载过本站文档，您可以点击这里二次下载。
4、如文档侵犯商业秘密、侵犯著作权、侵犯人身权等，请点击“版权申诉”（推荐），也可以打举报电话：400-050-0827(电话支持时间：9:00-18:30)。

几种零件的热处理实例（Examples of several parts of heat treatment）

几种零件的热处理实例（Examples of several parts of heat treatment） Example of gear heat treatment I. working conditions, materials and heat treatment requirements 1. conditions: low speed, light load, and no shock Requirements: HT200, HT250, HT300, stress relieving annealing 2. conditions: low speed ( 1m/s), light load, such as lathe, slide, gear and so on Requirements: 45, quenching and tempering, HB200-250 3. conditions: low speed, medium load, such as the standard series reducer gear Requirements: 45 40Cr, 40MnB (5042MnVB) conditioning, HB220-250 4. conditions: low speed, heavy load, no impact, such as machine tool spindle box, gear Requirements: 40Cr (42MnVB) quenching, medium temperature tempering, HRC40-45 5. conditions: medium speed, medium load, no heavy impact, such as machine tool spindle box, gear Requirements: 40Cr, 40MnB, 42MnVB quenching and tempering or normalizing, induction heating, surface hardening, low temperature tempering, aging, HRC50-55 6. conditions: medium speed, medium load, or low speed, heavy load, such as the secondary gear in the lathe transmission Requirements: 45 high frequency quenching, tempering at 350-370 DEG C, HRC40-45 (without high frequency equipment, can use rapid heating tooth surface quenching) The 7. condition: medium speed and heavy load Requirements: 40Cr, 40MnB (40MnVB, 42CrMo, 40CrMnMo, 40CrMnMoVBA) quenching, medium temperature tempering, HRC45-50. 8. conditions: high speed, light load or high speed, medium load, small gear with impact Requirements: 15, 20, 20Cr, 20MnVB carburizing, quenching, low temperature tempering, HRC56-62.38CrAl, 38CrMoAl nitriding, nitriding depth 0.5mm, HV900 9. conditions: high speed, medium load, no heavy impact, such as spindle of machine tool Requirements: 40Cr, 40MnB, (40MnVB) high frequency quenching, HRC50-55. 10. conditions: high speed, medium load, impact, complex shape and important gear, such as automobile transmission box The 20CrMnTi has high hardenability, low sensitivity to overheating,