配合比资料《配制c50桥梁混凝土》（Mixing ratio data C50 bridge concrete）.docVIP

配合比资料《配制c50桥梁混凝土》（Mixing ratio data C50 bridge concrete） This article is contributed by mybestdna DOC documents may experience poor browsing on the WAP side. It is recommended that you first select TXT, or download the source file to the local view. 1, the raw materials of the 1.1 aggregate concrete aggregate concrete volume accounted for about 3/4 of the volume, the volume is quite large, so the quality of aggregates on concrete technical performance and production costs have certain effect, in the preparation of C50 concrete, the aggregate gradation, strength, surface features, particle the shape, impurity content, water absorption rate, must be carefully inspected, strict selection. So as to make it meet the performance requirements of C50 concrete technology, but also can reduce the cost of concrete. 1.1.1 fine aggregate sand material quality, mixture effects more than C50 concrete workability than coarse aggregate to the preferred. Good gradation of river sand or river sand. Because the river sand or river sand is relatively clean, containing less sludge, more quartz particle content in sand, gradation can generally meet the requirements. The mountain sand cannot be used in mountain sand Containing a large amount of mud weathering and contains more soft particles. The fineness modulus of sand should be controlled in more than 2.6, the fineness modulus is less than 2.5, concrete mixing is too thick, the construction is difficult to vibration, and the fine sand, and easy to meet the same requirements, increase water consumption. This mud not only increase the cost of concrete, and the influence of technical performance of concrete, such as the durability of concrete, shrinkage cracks. The sand is too coarse, the fineness modulus is more than 3.3, easily lead to segregation transportation pouring process of fresh concrete and water poor, optimal control in 2.6~2.8 between the inherent quality and appearance the quality of.C50 pump which affect concrete concrete fi