带约束拉杆方形薄壁钢管竹胶合板组合空芯柱轴心抗压性能.doc

带约束拉杆方形薄壁钢管/竹胶合板组合空芯柱 轴心抗压性能 赵卫锋1，屈鹏1，周靖2*1 湘潭大学土木工程与力学学院，湘潭 411105；2. 华南理工大学亚热带建筑科学国家重点实验室，广州 510640 摘 要：为解决方形薄壁钢管/竹胶合板组合空芯柱（SBCC）抗压易开胶失效的问题，提出一种新型的带横向约束拉杆的方形薄壁钢管/竹胶合板组合空芯柱（SBCCB）。对9根SBCCB进行了轴心试验，截面尺寸、长细比和组合方式与有极限压应力进行比较。结果表明：设置约束拉杆可有效的开胶破坏，改变极限破坏模式，显著提高极限承载力极限压应力极限压应力。 关键词：竹胶合板；薄壁方钢管；约束拉杆；组合空芯柱；轴心抗压；极限承载力 中图分类号: TB332；TU366.1 文献标志码: A Axial compression behavior of square thin-walled steel tube/bamboo plywood composite hollow column with binding bars Zhao Weifeng1, Qu Peng1, Zhou Jing2, Long Zhilin*1 (1. College of Civil Engineering and Mechanics, Xiangtan University, Xiangtan 411105, China; 2. State Key Laboratory of Subtropical Building Science, South China University of Technology, Guangzhou 510641, China) Abstract：A new type of square, thin-walled steel tube/bamboo plywood composite hollow column with binding bars () was proposed to solve the issue that the general thin-walled steel tube/bamboo plywood composite hollow column （SBCC）was liable to the glue failure under compressive load. 9 were used to perform the axial compression tests. The failure modes of SBCCB loaded were investigated, and the influences of the net cross-sectional area, slenderness ratio and sectional combination mode of SBCCB on the crack load and ultimate bearing load of SBCCB were analyzed. The ultimate compressive stress of SBCCB was compared to that of the existing SBCC. The results indicate that the compressive damage of SBCCBs are primarily the broken damage to bamboo plywood material and the glue failure between the matrix interfaces at the end of column and the middle of column between binding bars. The ultimate bearing capacity is not only related to the net cross-sectional area and slenderness ratio, but also related to the sectional combination mode of SBCCB. The binding bars can effectively suppress the glue failure, change the ultimate failure mode and significantly improve the ultimate carrying capacity of SBCCB. Compared with the SBCCs, the ultimate compressive stress o