大间隙高强度胶粘剂在粘接石英陶瓷与低膨胀合金中的-宇航材料工艺.PDF

大间隙高强度胶粘剂在粘接石英陶瓷 与低膨胀合金中的应用 蒋海峰 　　周 　丽 　　张万良 (上海无线电设备研究院 ,上海 　200090) 文 　摘 　论述了使用硅凝胶粘接石英陶瓷材料与低膨胀合金 ,并通过采取减小内应力的方法 , 以使其能 提高强度且耐高温 。结果表明:在石英陶瓷与低膨胀合金的粘接过程中 ,该硅凝胶涂布方便 。在常温下 ,压 剪强度为 5. 18 MPa ;在 200 ℃的高温下 ,保温 5 min ,压剪强度仍可达 3 . 22 MPa 。它的强度及耐高温性能完全 符合应用要求 。 关键词 　内应力 ,大间隙 ,硅凝胶 Applications of Big Gap and High Strength Adhesive in Adhering Quartz Ceramic and Low Expansion Alloy Jiang Haifeng 　　Zhou Li 　　Zhang Wanliang ( Shanghai Wireless Equipment Academey , Shanghai 　200090) Abstract 　Applications of silicone adhesive for adhering quartz ceramic and low expansion alloy , and measures for reducing internal stress to obtain high strength and high temperature performance are discussed . It is indicated that the silicone adhesive is easy to smear in adhering quartz ceramic and low expansion alloy . Its strength strength is 5. 18 MPa under normal temperature ; its shear strength is still up to 3 . 22 MPa at 200 ℃within 5 min . Its strength and high temper ature performance are completely satisfied in the applications of spaceflight . Key words 　Internal stress , Big gap , Silicone adhesive 1 　概述 热应力大小正比于温度变化 、胶粘剂与被粘物线膨 石英陶瓷材料与低膨胀系数合金 ,两者的粘接 胀系数的差别以及粘接材料的弹性模量 。为了避免 存在不少问题 ,其中胶接过程中内应力是影响胶接 热应力 , 国外一般采用模量低延伸率高的柔性胶[2 ] , 强度和耐久性的重要因素之一 。内应力来源有两 使热应力能通过胶粘剂的变形释放出来 ,并通过增 个[ 1] : 大粘接间隙来降低异种材料产生的内应力 。如果小 ( ) 1 胶粘剂固化过程中由于体积收缩产生的收 间隙粘接 ,则粘接强度高 ,高温时内应力大 ,存在可 缩应力 ; 靠性隐患 。 (2) 胶粘剂和被粘物线膨胀系数不同 ,在温度变 另外 , 由于石英陶瓷与低膨胀合金的膨胀系数 化时产生热应力 。 相差很大 ,胶粘剂的选择