abs电镀（abs电镀） Five major problems of ABS plastic electroplating quality This article comes from: Assistant forum Proe tutorial Author: Super meter date: 23:33 yesterday read: 22 people print collection ABS, plastic plating, quality The quality of plastic electroplating is not only closely related to the electroplating process and operation, but also has great influence on the 5 aspects of material selection, structural design, plastic mold, plastic forming process and post-processing technology. 1.1 internal stress test The sample was dipped in glacial acetic acid at 25 DEG C for 3min, and the internal stress was judged by the degree of white on the surface of the specimen. The greater the internal stress, the more serious the white phenomenon. This method can approximately illustrate the internal stress. Determination of peel strength of 1.2 coating Determination of peel strength with peeling method: cut out 10mm wide strip in the specimen, pry the end of 30 ~ 40mm in the direction perpendicular to the surface of the coating (90 #176; #177; 5 #176;) with tensile machine stripping. 1.3 test of coating adhesion by high and low temperature impact test The method was proposed by the society of plastic electroplating workers in West Germany. The method is simple and reproducible. The specific process is: 80 degrees in #177; high temperature hot water bath 5 DEG C in insulation 1H, remove and add 5 C #177 in no more than 30s time; low temperature water bath 5 DEG C in leaching of 30s, and then transferred to the hot water bath, after 3 cycles, such as coating blistering, peeling, no hair wrinkle defects such as deemed qualified. 2.1, material selection can be used for electroplating a lot of plastic, but the processing performance of various materials, mechanical properties, material costs, electroplating costs, electroplating difficult, dimensional accuracy and so on are very different. ABS plastic has excellent comprehensive properties. It is widely used and is easy t