聚羧酸高效缓凝减水剂对混凝土耐久性影响.docVIP

聚羧酸高效缓凝减水剂对混凝土耐久性影响摘要：本文通过结合笔者从事混凝土耐久性及减水剂研究的相关工作经验，简要地概述了聚羧酸高效缓凝减水剂的结构特点及其优点；同时详细地分析了聚羧酸高效缓凝减水剂对商品混凝土的抗渗性、抗冻融性、抗硫酸盐腐蚀性、抗氯盐腐蚀性、抗钢筋锈蚀、钢筋-混凝土粘结强度等耐久性的影响。最后，结合工程实例，介绍了聚羧酸高效缓凝减水剂的工程应用技术。 关键词：聚羧酸高效缓凝减水剂；混凝土；耐久性；工程应用技术 Abstract: in this article, through combining the durability of concrete and water reducing agent engaged in the study of relevant work experience, this paper briefly summarizes the clustering of carboxylic acid efficient slow the structure characteristics of the water reducing agent and its advantages; And detailed analysis of carboxylic acid efficient together on water reducing agent for goods of concrete penetration-proof quality, freezing-thawing resisting sexual resistance, corrosion resistance, anti-chlorine sulphate corrosive, resistance to corrosion of reinforcement, steel and concrete bonding strength of durability influence. Finally, combined with engineering example, the paper introduces the high efficiency of carboxylic acid together on reducing agent of project application technology. Keywords: gather water reducing agent of carboxylic acid efficient slow; Concrete; Durability; Engineering application technology 中图分类号：TU37文献标识码：A 文章编号： 1． 引言 硬化混凝土的耐久性包括抗渗性、抗冻融性、抗硫酸盐腐蚀性、抗氯盐腐蚀性、钢筋锈蚀、钢筋―混凝土粘结强度等几个方面。通常，适度引气、水灰比低的硬化混凝土在严酷环境条件下的耐久件良好。掺用高效减水剂可起到适度引气、降低水灰比的作用．所以掺入高效减水利可提高硬化混凝土耐久性，至少可以说，高效减水剂的掺入不会对耐久性产生不利影响。 2． 聚羧酸高效缓凝减水剂概述 聚羧酸高效缓凝减水剂对是以带有羧基、磺酸基、羟基、聚氧化烯基链节等活性基团的不饱和可聚合单体为原料，经直接共聚法、聚合后功能化法或原位聚合与接枝法制得的一些全新的高性能减水剂。该类减水剂特有的梳形分子结构赋予其低掺量、高碱水、保水及增强效果好等特点，此外，还可以通过“分子结构设计”、控制合成工艺参数等手段，调整其分子结构，分子量及其分布，从而实现高性能化，因此，该类减水剂已成为高效减水剂的研发热点和重点之一，并代表着高效减水剂的发展趋势。 聚羧酸高效缓凝减水剂的优点：（1）掺量低而分散性能好，通常在胶凝材料用量的0.2%~0.5%的掺量下，混凝土减水率可达30%以上，且不离析，不泌水。（2）保坍落度性能好，混凝土90~120min内坍落度基本无损失；（3）与水泥、掺合料及其他外加剂的相容性好。（4）可有效地提高用于替代波特兰水泥的粉煤灰、磨细矿渣等掺合料的掺量，从而降低混凝土成本。（5）可根据不同设计要求，用于配制普通、高强、超高强、高流动性、早强、大体积混凝土等。（6）制备过程中不使用甲醛，因而不会对环境造成污染。 3． 聚羧酸高效缓凝减水剂对混凝土耐久性的影响分析 3.1 抗渗性 混凝土的抗渗性与其孔隙率及孔结构有关。混凝土内孔隙按孔径大小大致可分为＜4~5nm、5~50nm、50~100nm及＞100nm四级。若孔径大于50nm的孔隙体积分数增大，则会对混凝土强度和抗渗性带来不利