高层建筑大体积混凝土基础裂缝研究控制.doc

高层建筑大体积混凝土基础裂缝研究控制摘要: 随着现代工程建设的快速发展,大体积混凝土在高层建筑工程中的应用日益广泛，由于水泥水化过程中释放的水化热会引起温度的较大变化和收缩的作用，产生的温度应力和收缩应力是导裂缝导致混凝土产生的裂缝的主要原因。本文比较系统的阐述了大体积混凝土的基本概念和其特点，并着重分析了大体积混凝土结构裂缝产生的机理和原因，从而总结出了控制混凝土产生裂缝的一些措施，避免裂缝的产生。 关键词:大体积混凝土，温度裂缝，控制措施 Abstract: with the rapid development of modern engineering construction, big volume concrete in high-rise building engineering of wide application, because the cement hydration process of the release of the hydration heat can cause great changes of temperature and shrinkage effect, produce the temperature stress and shrinking stress cracks in the concrete is the main cause of cracks generated. This paper makes a comparison of the system are introduced the basic concept and its concrete characteristics, and focusing on the analysis of the mass concrete structural cracks mechanism and causes, and summarizes the concrete crack control some measures to avoid the cracking of the. Keywords: mass concrete, temperature crack, control measures 中图分类号： TV544+.91文献标识码：A 文章编号： 一、前言 随着我国高层建筑的开发建设，大体积混凝土结构已成为高层建筑的重要组成部分，高层建筑往往受到较大载荷的影响，一般需要大体积混凝土进行浇筑。与普通混凝土的有所不同，大体积混凝土设计的强度要高，截面尺寸较大，浇注量很大，使得水泥产生的水化热引起的温度变化和收缩作用，极易产生变形和裂缝，直接的影响混凝土的强度和质量，因此，为了有效地大体积混凝土产生裂缝，需要采取一些措施控制裂缝的产生，从而保证高层建筑结构的质量安全。 二、大体积混凝土的定义 目前关于大体积混凝土的定义，尚无统一的定论。美国混凝土协会的定义为：任何就地浇筑的混凝土，其尺寸要大，同时要解决好水化热以及由此引起的体积的变形问题，最大程度上减少混凝土产生裂缝。而日本建筑学会规定：结构断面的尺寸至少为800mm,同时由水化热引起的混凝土内部的温度，预计比其表面温度要高25℃。 我国对大体积混凝土的定义还不严格，其设计规程认为：混凝土结构物的实体的尺寸要大于等于1000mm,或者由于水化热引起的内外表面的温度之差引起混凝土的开裂。大体积混凝土除了尺寸大之外，更重要的是混凝土内部的水化热不容易散失，在外界环境或是混凝土内力的作用下，容易导致温度收缩裂缝的产生，因此，仅用混凝土的几何尺寸来表征是不够严密的。同样情况，仅用水化水化热引起的内外表面的温度之差定义也是不够科学的。因此，对于大体积混凝土的定义要准确度的反映混凝土的工程的性质，首先混凝土结构的几何尺寸要大，其次必须采取措施解决由水化热引起的内外温差导致混凝土的开裂问题，以控制裂缝开裂的最小程度，这种混凝土就称之为大体积混凝土。 三、大体积混凝土基础的特点 (1) 大体积混凝土的结构尺寸大、用量多、工程条件极为复杂以及施工技术难度高等特点。由于大体积混凝土的结构尺寸较大，外力作用引起裂缝的可能性可以忽略，然而混凝土的水化所引起内外的温差变化以及混凝土的收缩作用，是导致混凝土开裂的主要原因。 （2）高层建筑中的大体积混凝土还具有：混凝土的强度级别要求较高，混凝土浇筑用量较多，使得容易产生收缩变形，同时，与坝体混凝土相比，其结构尺寸较小，使得水化热的温度上升较快，散热降温也很快，混凝土的降温和收缩是导致混凝土开裂的主要原因。 四、大体积混凝土结构设计与施工的特点 大体积混凝土