Standard Test Method for Mode I Interlaminar （我层间的标准测试方法模式）.pdfVIP

Designation: D 5528 – 01 (Reapproved 2007)´3 Standard Test Method for Mode I Interlaminar Fracture Toughness of Unidirectional Fiber-Reinforced Polymer Matrix Composites1 This standard is issued under the fixed designation D 5528; the number immediately following the designation indicates the year of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A superscript epsilon (´) indicates an editorial change since the last revision or reapproval. ´1 NOTE—Added research report reference to Section 14 editorially in March 2008. ´2 NOTE—Corrected Eq. 3 in July 2008. ´3 NOTE—Eq. 3 was rewritten for clarification in August 2009. 1. Scope 1.1 This test method describes the determination of the opening Mode I interlaminar fracture toughness, GIc, of con- tinuous fiber-reinforced composite materials using the double cantilever beam (DCB) specimen (Fig. 1). 1.2 This test method is limited to use with composites consisting of unidirectional carbon fiber and glass fiber tape laminates with brittle and tough single-phase polymer matri- (a) with piano hinges (b) with loading blocks ces. This limited scope reflects the experience gained in FIG. 1 Double Cantilever Beam Specimen round-robin testing. This test method may prove useful for other types and classes of composite materials; however, D 3171 Test Methods for Constituent Content of Composite certain interferences have been noted (see 6.5). Materials 1.3 The values stated in SI units are to be regarded as the