The Study of Proper Time Range Welding to （适当的时间范围焊接的研究）.pdf

Proceedings of the 1st WSEAS International Conference on MATERIALS SCIENCE (MATERIALS08) The Study of Proper Time Range Welding to Resistance Spot Welding for Mild Steel S. NANSAARNG*, P. PEARSURA Department of Production Technology Education, Faculty of Industrial Education and Technology King Mongkut’s University of Technology Thonburi 126 Pracha Uthid Rd., Bangmod, Troong Kru, Bangkok 10140. THAILAND Abstract: - This research use the mechanical property and macro testing to identify the proper time rang for current flow. The specimen tested was 1 mm. thickness in mild steel. The welded specimens were tested by Tensile Shear testing following JIS Z 3136: 1999 and Macro Structure testing following JIS Z 3139:1978 Subsequently, the analyzed data were compared with standard JIS Z 3140. The results show that the suitable current flow is 8 to 10 cycle tensile shear test5.33 kN to 6.39 kN nugget size 4.92 mm. to 5.66 mm. . It can be concluded that this technique can be applied to monitor the processes and the quality of resistance spot welding. Key- Words: - Resistance spot welding, Mechanical Property, Macro Structure Testing 1 Introduction Resistance spot welding is a type of welding process in 2 Equipments and Experiment Method use by automotive industry, furniture, building 1. The specimen tested was cast steel which passed cold construction and electronics with the most common polling process with a thickness of 1mm. Specimen application because it can weld the workpieces speedily preparation following JIS Z 3136: 1999 by cutting with less thermal effect, strong enoug