多次烧结遮色瓷对金瓷修复体结合强度影响的试验研究陈林李春林.DOC

多次的实验研究 [摘要]目的 探讨遮色瓷不同烧结次数对镍铬金瓷修复体结合强度的影响。方法 采用剪切强度测试测多次运用1、35、7、9Cr、O3次。 [关键词] 金瓷修复体 ; 遮色瓷; 烧结 ; 结合强度 The influence of multiple fireing opaque on the bond strength of porcelain-fused-to- metal restoration Chin Lin，Li Chunlin, Liu Jianguo, Wang Hang,Li Jieyi . Affiliated Stomatological Hospital of Zunyi Medical college，Zunyi, 563003，China） CChin Lin，Tel：0852-8635729， E-mail: cwl0@ [Abstract] Objective To investing at the effects of multiple fireing opaque on the bond strength of porcelain-fused-to-metal(PFM) restoration. Methods Porcelain-metal bond strength of multiple fireing opaque were measured with shear bond strength assay, and Porcelain-metal interface were test thought elecctron probe micro- analyzer (EPMA). Results The shear bond strength was apt to decrease with the increase of repeated fireing, significant difference (P＜0.05)were found between 1, 3and 5,7, 9 times;. Moreover, the content of Cr, O in the PFM interfacing increased as well. Conclusion 3 times fireing opaque layer or more may decrease the bond strength of PFM restoration. [Key Words]Porcelain-fused-to-metal; restoration; Opaque Fireing Bond stren- gth 金属烤瓷修复体以其较高的硬度、美观的色泽而得到患者的普遍喜爱，是牙体缺损及牙列缺损最理想的修复体之一。金瓷修复体失败的主要原因是瓷层失败（占53%），即将金瓷界面产生应力而导致金瓷结合力下降和瓷层断裂或隐性裂纹。因此，研究金瓷界面变化，探讨瓷层失败原因，增强金瓷结合力，提高烤瓷修复体质量，一直是临床烤瓷修复面临的重要课题。本实验拟利用万能测力机测量多次烧结遮色瓷层后的金瓷修复体剪切强度，以期找出遮色瓷合适的烧结次数范围,并通过X射线衍射分析仪测试主要元素的扩散情况，从微观上分析、探讨金瓷结合强度变化的原因，为金属烤瓷修复体的制作提供实验依据。 [通信作者] 陈林，电话：0852-8635729 E-mail: cwl0@ 材料和方法 1.材料与设备：松风烤瓷非贵金属镍铬合金、松风烤瓷粉(遮色瓷、体瓷 颜色A2，松风株式会社，日本），高温包埋料及180μm氧化铝砂(Dentsply公司，德国) DEZ-50 高频离心铸造机（天津医疗设备厂，天津），PHOENIX-7型电脑烤瓷炉（CERANCO公司，美国）, Instron-4302万能测力机(INSTRON公司,英国),游标卡尺(精度0.02mm),千分尺(精度0.01mm，上海精密仪器设备公司, 上海)。 2.金瓷试件的制作：制作边长8mm×8mm×8mm的蜡型45个，蜡型表面清洁光亮，由同一人对蜡型进行包埋铸造。铸造后把试件打磨修整成5mm×5mm×5mm的立方体且将表面磨光（使用金刚钻磨头），再用粒度为180μm的Al2O3砂喷砂（压力0.15Mpa/min）,而后用75%的乙醇超声清洗20min,吹干，表面预氧化2min。在试件上精选一个面，其上用有机玻璃模具控制遮色瓷的上瓷面积为9mm2，厚度为0.3mm，放入烤瓷炉中由650℃烧烤至960℃，放在炉口预干燥5min。试件遮色瓷面再用180μmAl2O3砂湿磨至遮色瓷厚度为0.2