紫金山低品位铜矿生物堆浸模拟研究探究.docVIP

紫金山低品位铜矿生物堆浸模拟研究 吴健辉 （紫金矿业集团股份有限公司，福建上杭 364200） 摘要：对紫金山低品位铜矿进行生物堆浸模拟试验。结果表明起始喷淋液浓度4.0 gL、矿石粒度-10 mm，浸出周期为181天，铜浸出率达到80%以上。片碱调节喷淋液pH沉矾除铁，采用不同喷淋制度抑制酸铁浸出是低品位铜矿生物堆浸未来重要研究方向。 关键词：低品位铜矿；矿物学；生物堆浸中图分类号：TF811 文献标志码：A 文章编号：1007-7545（201）0-0000-00 Research of Biological Heap Leaching Analog of Zijinshan Low-grade Copper Ore WU Jian-hui (Zijin Mining Group Co., Ltd, Shanghang 364200, Fujian, China) Abstract：Zijinshan low-grade copper ore was simulation tested by biological heap leaching. The results show that copper leaching rate is 80% above under the optimum conditions including total iron concentration of initial spray solution of 4.0 g/L, particle size of -10 mm, and leaching duration of 181 days. Key focus should be paid on adjusting pH value of spray solution with sodium hydroxide to remove iron and inhibiting leaching of iron by different spray process for biological heap leaching of low-grade copper ore. Key words：low-grade copper ore; mineralogy; biological heap leaching 紫金山铜矿属于低品位次生硫化铜矿，黄铁矿含量及硫铜比高，耗酸脉石少，在开采和生产过程中会产生大量的矿山酸性废水[1]。目前铜品位大于0.4%的矿石进入浮选系统，铜品位低于0.4%的矿石进入生物堆浸提铜系统[2-]。随着开采的不断进行，铜矿石品位不断下降，对生物堆浸工艺进行优化势在必行。 开展紫金山低品位铜矿堆浸过程模拟试验，考察堆浸过程喷淋液种类、喷淋液铁离子浓度、喷淋工艺、矿石粒度等因素对硫化相氧化率、铜浸出率的影响，为紫金山低品位铜矿资源化利用及铜矿勘探提供技术依据。 1 试验原料及方法 1.1 试验原料 试验所用原料为紫金山868平台北部低品位铜矿，原矿破碎至-30 mm。 1.2 试验方法 铜矿石生物柱浸试验在Φ160 mm×1 000 mm的PPR材质柱子中进行。柱内插入热电偶测定柱内温度，通过温控仪实现柱体温度的调节与控制；利用蠕动泵控制溶液喷淋强度。定期测量浸出液体积、pH、电位离子浓度，浸出液铜离子达到一定浓度萃取处理，萃余液调整pH后返回喷淋。 根据现场生产工艺参数，固定喷淋强度为20 L/m2·h)，前70天连续喷淋，70天后每周喷淋2天，柱浸温度为常温，喷淋液pH 1.31.8。试验条件如表1所示。 表1 柱浸试验条件 Table 1 Test conditions of column leaching 柱号 矿石粒度/mm 喷淋液 喷淋工艺中和剂 种类 Fe3+/g·L-1) 1 -10 萃余液 12.0 循环 前120采用石灰调碱，后期以氢氧化钠调碱石灰调碱 2 12.0 循环 3 硐坑水 1.3 不循环 4 萃余液 1.3 循环 5 4.0 循环 6 -30 硐坑水 1.3 不循环 7 萃余液 4.0 循环 2014-08-25 基金项目：国家自然科学基金资助项目 作者简介：吴健辉(1974-)，男，福建光泽人，硕士，高级工程师. 2 矿石性质分析 2.1 化学成分 矿石＜0.01 g/t3.82%，铜含量为0.15%，品位较低4.10%，其中S2- 3.21%、S6+ 0.25%，说明矿石中铜大部分以蓝辉铜矿、铜蓝形式存在且矿石含有较高含量铝7.72%）及微量砷0.013%）。由铜、铁、硫含量可推断矿石中黄铁矿含量较高。2.2 粒度 为研究低品位铜矿中铜的粒度分布特征，对破碎后的原矿进行粒度筛析试