烙铁头资料（Soldering iron data）.doc

烙铁头资料（Soldering iron data） Lead free soldering iron tip: Is the use of lead-free soldering iron Tsui copper (copper as the main thermal conductivity fast, not easy to deformation), then on the basis of the original plating a layer of iron layer (iron corrosion), the iron layer and then coated with a layer of nickel (Ni as appearance). Relevant knowledge: First, the problem of lead-free soldering iron Tsui: 1, high melting point, tin wire is not easy to melt; 2, iron Tsui consumption faster; 3, tip oxidation quickly; 4, wettability, reduced ductility; 5, prone to tin whisker, short circuit and so on. Two, iron Tsui consumption principle: 1, the iron material is in tin tin wire melting iron Tsui, erosion; 2 coating of iron and tin compounds; 3, lead-free solder wire in the tin content increased, the increase of the corrosion; 4, lead-free welding, temperature increase, increase the tip corrosion (350 C after each increase of 30 DEG C tip increased consumption of 1-2 base). Note three: when using lead-free solder, temperature management 1, tip is very important; 2, the use of heat recovery of electric iron heat resistance; 3, selected the appropriate electric iron; 4, as far as possible by the low temperature (350 DEG C) to carry out welding work; 5, thoroughly implement the maintenance tips the The soldering iron head is mainly composed of four kinds of metal materials: copper, iron, nickel, chromium and tin. Copper, as a heat conductor, is the chief component of the iron head. Accounted for about 85% of the iron head material, the thermal conductivity of copper, iron head is conducive to rapid warming, good iron head are made of copper, but some manufacturers use brass, in order to reduce costs, but also reduce the thermal effect of the soldering iron head. Iron - corrosion resistance, is the key factor affecting the service life of the iron head. The utility model has the advantages that the iron head is plated with iron, the crystal structure is fine and dense, the