树脂固化放热曲线测试方法的改进（Improvement of test method for exothermic curve of resin curing）.docVIP

树脂固化放热曲线测试方法的改进（Improvement of test method for exothermic curve of resin curing） Abstract: the test method of heat release curve of resin curing has been improved by means of computer aided multi-channel data collector. The method can be used for tracking and controlling the whole curing process, and has the advantages of simple operation and high efficiency. The utility model not only saves the expenditure of the experimental equipment, but also reduces the error and inconvenience existing in the current experiment. The improved experimental method has certain popularization value in the current experimental teaching of University composite materials. Key words: experimental method; curing exothermic curve; teaching reform; ???? DSC with cure exothermic curve (DSC) test, DSC curve can be obtained by testing the related resin curing reaction starting temperature, peak temperature, final temperature and total heat release and heat enthalpy and a series of important thermodynamic parameters, so as to provide theoretical and experimental guidance for processing composite materials. Because DSC equipment is expensive and the quantity is seriously insufficient, students have little opportunity to do experiments themselves. Based on years of practical teaching and research experience, the experiment has made a great improvement from the equipment to the method. The experimental results show that the improved experimental method has the characteristics of less equipment input, multiple machines, simultaneous operation, high efficiency and quick performance. First, DSC method, experimental methods, status Curing is the result of a chemical reaction between the active groups, resulting in cross-linking between molecules. In the curing process of the resin, the thermal effect is accompanied by different degrees of heat. The mechanism and process of the curing reaction of polymer matrix composite can be analyzed by testing the exothermic curve of the resin during the curing re