.24.灰铸铁试样低频内耗特性的测试与分析.pdfVIP

2010 中国铸造造周论文集 灰铸铁试样低频内耗特性的测试与分析 彭金花，汤虎，陈萌，杨弋涛 （上海大学材料科学与工程学院,上海 200072） 摘要：运用低频内耗谱分析和光学显微镜观察，探究了灰铸铁阶梯试样在不同孕育处理工艺下的微观组织 与内耗的相关性。实验结果表明，随着温度的升高，内耗值先增加后减小；冷却速度较大而得到菊花状石 墨时内耗值最小；石墨面积越大，内耗值就越大，石墨越细小，内耗值就越小。试验结果可望用于灰铸铁 减振特性的科学表征。 关键词：灰铸铁；组织；内耗 Measurement and Analysis on Low Frequency Internal Friction Characteristic of Gray Iron Specimen Peng Jinhua, Tang Hu, Chen Meng, Yang Yitao (School of Materials Science and Engineering, Shanghai University, 200072) Abstract: The use of low frequency internal friction spectrum analysis and optical microscopy study is to research into the correlation between microstructure and internal friction of gray cast iron samples in different inoculation treatment process. The results showed that as the temperature increased, internal friction values increased and then decreased; when cooling rate was large, graphite was daisy-like, and the internal friction value became the minimum; the larger the area of graphite, the higher internal friction value, the more small graphite, the smaller the internal friction value. The results were expected for the scientific characterization of damping characteristics in gray cast iron. Key words: Gray cast iron;Microstructure;Internal friction [1] 内耗测试技术 在现代材料的研究和开发中占有重要的作用和不可替代的地位，它是一种灵敏度高的 无损检测方法，能反映固体内部原子尺度上各种结构缺陷的组态及其交互作用。内耗作为描述材料减振特 性的关键指标之一，被用于评价灰铸铁件的减振性。灰铸铁是一种十分经济有效的高阻尼金属材料，国外 的报道[2,3] [4] 以及国内的报道 都是提高碳当量使石墨片数量以获得高阻尼性能，但都主要集中在对石墨分布 的定性分析，并没有给出定量描述，因而很有必要用石墨的面积及周长等参数来分析灰铸铁的内耗性能的 微观机理。 本文采用 LMA-1 低频力学谱仪对灰铸铁内耗进行测试，并通过金相检测，进一步分析了石墨的周长， 面积等内部参量对内耗的影响；以及选择不同的孕育处理工艺对金相及内耗的影响。 1 试验材料和方法 1.1 实验材料的制备 在企业生产条件下进行熔炼浇注实验，当感应电炉熔炼中灰铸铁的熔液温度升至1413℃，取炉前光谱 试样，调整成分至目标值后，出一小