RH真空喂硅钙线生产实践.PDFVIP

RH 真空喂硅钙线生产实践 黄成红 邓品团 张洪钢 林利平 （武钢股份炼钢总厂，湖北武汉 430083） 摘要 RH 喂硅钙线处理是武钢股份炼钢总厂二分厂 2 年多来使用较多的一种改善钢质的成熟工艺。生产实践表明，RH 结束 后喂硅钙线的收得率与喂线速度、喂线钢种、喂线量、喂线后的吹氩强度大小等有关；喂硅钙线应处理好增 Si、增B、增N 对钢种成分的影响，避免 Si、B、N 出格改钢；喂硅钙线能改变品种钢中夹杂物的形态，并提高轧后冲击韧性。 关键词 喂硅钙线 实践 Practice of RH Feeding Silicon Calcium Line Huang Chenghong, Deng Pingtuan, Zhang Honggang, Lin Liping (shares of wisco steelmaking general factory,，HuBei Wuhan 430083) Abstract Feeding silicon calcium line processing at RH is a kind of normal process for improving steel quality.Shares of wisco steelmaking general factory production practice shows that after the vacuum rate of feeding silicon calcium line closed to hello linear velocity ，hello linear varieties ，hello linear amount and blow argon strength; Feeding silicon calcium line should handle well influence of adding silicon ，adding boron , adding nitrogen and avoid silicon ，boron and nitrogen commute; comparing with mould feeding RE line , RH feed silicon calcium line has advantage of low cost ; Feeding silicon calcium line can change form of inclusions in varieties steel and enhance impact toughness after steel rolling . Key words feeding silicon calcium line practice 为了满足新品种的研发需要，武钢股份炼钢总厂二分厂（以下简称炼钢二分厂）2011 年 3 月在 2 台 RH 各配备了 1 台喂丝机，对新试品种进行喂硅钙线处理。2011 年 6 月结晶器喂 Re 丝的的价格由 50 元/ 公斤上涨到 209 元/公斤，且居高不下。鉴于结晶器喂 Re 丝作用主要是改变钢中硫化物夹杂的形态，提高 轧后冲击韧性。从降成本的角度考虑，公司决定炼钢二分厂采用 RH 喂硅钙线工艺替代了结晶器喂 Re 丝 的工艺。结晶器喂Re 丝的钢种多达 25 个，且产量偏大，导致炼钢二分厂 RH 喂硅钙线工艺的快速进步。 钢水进行钙处理的目的是改善钢质。通过钙处理使 Al2O3 转变为 12CaO ·7 Al O 低熔点物质，加速 2 3 上浮，减少 Al O 夹杂，并使 Al O 由串状变为球状铝钙酸盐不变形夹杂；通过钙处理使硫化物（FeS ， 2 3 2 3 MnS ）转变为球状 CaS，从而改善钢板的冲击韧性；通过钙处理还可以改善钢水的浇铸性能，防止中包塞 棒和浸入式水口被 Al O 夹杂堵