乌克兰G0R精炼转炉技术综述 年产30万吨不锈钢连铸坯 的GOR转炉工段施工设计介绍 乌克兰国家冶金学院萨道夫尼柯（教授）? 冶金工业规划研究院刘晓民（教授） ?????????????????? 维 利 奇科（教授）???????????????????? 鹿?? 宁(硕士) ?? 摘要：通过对国内一座60吨GOR转炉施工设计的简要介绍，论述了GOR转炉的基本结构、工作原理、工艺的优势。从这种炉子冶炼不同品种的不锈钢的技术经济指标的介绍，可以认为这是一种投资节省、冶炼成本低、钢水质量好的先进工艺技术，与国内目前普遍采用的其它种类的不锈钢精炼工艺相比，具有比较强的市场竞争力。 Abstract: The paper dissertates the basic configuration, mode of operation, technical superiority of GOR converter by brief describing the construction design of a 60 tons GOR converter in China. According as the introduction of technical and economical indices of GOR converter in smelting different kinds of stainless steel, it is reputed that the converter has advanced process engineering with the following advantages: economizing invest, low smelting cost and good molten steel quality. Compared with the refining practice techniques adopted by other converters using widely in China, GOR converter possesses stronger market competence. KEY: 60t GOR converter?smelting stainless steel market competence. 牋 国内一家不锈钢公司经过考察和对比，确定建设一座60吨GOR转炉作为30万吨/年不锈钢炼钢车间的精炼炉。这个车间采用一座60吨电炉 --- 一座60吨GOR转炉二步法冶炼ASTMA276-92标准规定的201（1Cr17Mn6Ni5N）、304(0Cr18Ni9)等不锈钢钢种，钢水经一套国产的板坯连铸机浇铸成板坯。该公司委托冶金工业规划研究院和乌克兰钛设计院承担精炼工段的设计、试车指导、生产20炉合格的不锈钢（成份和温度合格率达到100%）任务。 ?? GOR精炼转炉技术是前苏联的第聂伯尔冶金学院和钢铁研究院合作开发的一种不锈钢冶炼工艺，在前苏联境内建设有1吨、5吨、10吨和60吨的GOR转炉不锈钢冶炼车间，目前乌克兰全国的不锈钢钢材都是利用这种炉子生产的钢坯轧制的。这种工艺是前苏联的专利技术，乌克兰独立后，被批准为乌克兰的专利技术。这次设计参考了扎波罗什特钢厂60吨GOR转炉15年的生产经验。但是中国冶炼不锈钢的原材料构成与乌克兰有很大差异，并且计算机技术的发展使这种工艺更容易实现冶炼过程的自动化控制，设计中进行了多项改进。?? GOR转炉是多种能源介质复合吹炼的底吹转炉，其供气管路可以向熔池吹入可调成份的氧气、氮气、氩气、天然气（或其它炭氢化合物）的混合气体。这种工艺具有如下一些优点： ―――冶炼周期为40-60分钟，高的生产率使这种工艺能做到以一当二，从而可以降低投资。 ―――工艺过程具有高的灵活性：可以用废钢和高炭铁合金、也可以用100%的不锈废钢（不另加合金）来冶炼不锈钢。 ―――根据成品钢中炭含量要求不同，氩气消耗6－13.5立方米/吨。 ―――这种工艺不但可以冶炼任何一种国际标准的不锈钢，还适用冶炼高级合金钢、低合金钢和炭素钢。 ―――GOR转炉可以很容易的实现合理的温度制度和造渣制度，包括5吨的小转炉也没有发生热量不足的困难。 ―――特殊的出钢口设置可以准确的控制炉渣进入钢包的数量，有利于钛等容易氧化的合金元素的合金化，也有利于对成品钢水进行调质。 ――在通过吹入氮气准确的控制含氮钢中的氮含量（达到溶解度及以下），精确度为±0.01%（质量）。 ――炉令高，降低了耐火材料消耗。 ――在最低氧化性条件下实现深度脱气，降低铅、锡等有色金属含量。 ――容易实现工艺过程再现，方便的实现工艺过程自动控制。 1.