浅谈建筑施工技术中钢筋混凝土裂缝问题.docVIP

浅谈建筑施工技术中钢筋混凝土裂缝问题 　　摘要：建筑行业是我国国民经济的重要支柱，是经济发展的主导力量之一，随着现在我国建筑行业的不断发展，建筑的质量问题就成了我们普遍关注的问题。在建筑施工技术中，钢筋混凝土裂缝的预防与控制是一个难题，同时它又十分广泛地存在建筑施工当中。文章结合建筑行业钢筋混凝土裂缝问题的处理现状和本人多年的工作经验，简单分析了钢筋混凝土裂缝问题，以期和同仁共同探讨，为我国建筑行业的发展贡献自己的一份力量。 关键词：钢筋；混凝土；裂缝养护；配料 Abstract:The construction industry is an important pillar of our national economy, is one of the leading force in economic development, with the continuous development of China’s construction industry, the construction quality problem has become our common concern. In the construction technique, reinforced concrete crack prevention and control is a difficult problem, at the same time it is very widely exist in building construction. Current treatment combined with reinforced concrete cracks in building industry and my years of work experience, a simple analysis of the cracks in reinforced concrete, in order to study with the colleagues, contribute to the development of China’s construction industry. Keywords:Reinforced concrete; crack; maintenance; ingredients 中图分类号：TU375 文献标识码：A文章编号： 因为混凝土的特质，导致混凝土凝结硬化过程中就有微裂缝存在，这样就造成了钢筋混凝土构件带裂缝工作的特点。因为，混凝土中含有一定比例的水泥石和骨料，这些材质在温湿度变化条件下能够产生不均匀的体积变形和膨胀，由于体积的增大，这些材质相互粘结在一起，又因为相互之间有一定的压力，在体积膨胀的同时还不能够自由变形，这就导致了水泥自身的抗拉强度增强，从而产生微裂缝。这是在混凝土构件前期就带有的裂缝。 一、混凝土产生裂缝的原因 混凝土产生裂缝的原因有不同的种类，根据具体情况来说，一般而言，混凝土裂缝的产生都是微裂缝发展而导致的。用混凝土内部构件来说明就是，如果混凝土材料在硬化过程中产生的变形约束所引起的内应力大于材料抗拉强度的话，就容易造成裂缝的产生。具体来说原因有以下几种： 1、构件受力、变形导致的缺陷和裂缝： 构件受力指的是在混凝土构件施工过程中，经过一些列的施工过程，构件承受的中心拉力、中心压力、受剪、受弯、受冲切、混凝土收缩、混凝土变形、板的混凝土收缩和温度变形等压力。不同的情况应该区别对待，一种是在钢筋混凝土中，钢筋承受拉应力，混凝土承受压应力；另一种是在素混凝土内和钢筋混凝上的边缘部位，混凝土就必须承担结构内出现的拉应力。我们在设计中的要求是，减少甚至不允许出现拉应力，但是在实际施工过程中，因为混凝土在冷却过程中，是由高温到低温的，这种温度的转变都会相应地产生内部拉应力。 2、环境因素的改变导致的缺陷和裂缝 在混凝土施工过程中的环境改变主要是指温度和湿度的改变、混凝土的结构不合理、混凝土的脆性和不均匀性、原材料质量不合格、构件模板变形等因素。混凝土构件多次受冰冻,即溶解循环作用，使混凝土中产生内应力，促进已有裂缝发展，结构疏松，表面龟裂,表层剥落或整体崩溃。 3、施工过程中违反操作规程而形成缺陷和裂缝： 违章施工的现象比较多，造成的缺陷和裂缝情况也比较多。这里简单列举几项比较典型的违反操作规程的现象： （1）塑性混凝土下沉被顶部钢筋所阻形成沿钢筋的裂缝； （2）混凝土振捣不密实出现蜂窝易形成各种受力裂缝的起点； （3）混凝土搅拌、运输时间过长使水分蒸发引起混凝土浇注时坍落度过低使得在混凝土体积中出现不规则的网状裂缝；