大体积混凝土裂缝控制技术要点探析 　　摘要：近年来，随着建筑高度越来越高，高层建筑底板厚度越来越厚，大体积混凝土底板由于度应力产生裂缝在工程实践中屡见不鲜，所以加强大体积混凝土的质量控制尤为重要，在对大体积混凝进行浇筑的时候，应该合理的安排好施工的程序，认真组织施工，从而有效的确保混凝土的整体质量。本文在此从裂缝产生的原因出发，提出了施工工程中防治裂缝应该注意的几个技术要点。 关键词：大体积；混凝土；裂缝；浇筑 Abstract: In recent years,along with thebuilding height increasing,the thickness of bottomof high-rise building more and morethick,large volume concrete slabdue to the degree of stresscracksit is often seen.In engineering practice,so it is important to strengthen the qualitycontrol of mass concreteis particularly important, whenthe large volumeconcretepouring,should be reasonable arrangements forthe constructionthe program,serious organizationconstruction,thereby effectivelyensuring the overallquality of concrete.This paperbased on thereasons of thecracks,and puts forward sometechniques of prevention and treatment of cracksin constructionshould pay attention to the. Key words: large volumeconcrete;crack;construction; 中图分类号：TV544+.91文献标识码： 文章编号: 前言：混凝土浇筑施工主要的技术与施工的难点就是在施工中防止混凝土浇筑体出现裂缝，并且造成大体积的混凝土开裂，其具体的原因就是由于混凝土浇筑体由于失水过多导致干燥、收缩和降温收缩，产生裂缝。 一、大体积混凝土裂缝产生的原因分析 大体积混凝土内出现的裂缝按深度的不同，分为贯穿裂缝、深层裂缝及表面裂缝三种。贯穿裂缝是由混凝土表面裂缝发展为深层裂缝，最终形成贯穿裂缝。它切断了结构的断面，可能破坏结构的整体性和稳定性，其危害性是较严重的;而深层裂缝部分地切断了结构断面，也有一定危害性;表面裂缝一般危害性较小。 大体积混凝土施工阶段所产生的温度裂缝，一方面是混凝土内部因素：由于内外温差而产生的;另一方面是混凝土的外部因素：结构的外部约束和混凝土各质点间的约束，阻止混凝土收缩变形，混凝土抗压强度较大，但受拉力却很小，所以温度应力一旦超过混凝土能承受的抗拉强度时，即会出现裂缝。这种裂缝的宽度在允许限值内，一般不会影响结构的强度，但却对结构的耐久性有所影响，因此必须予以重视和加以控制。 产生裂缝的主要原因有以下几方面： 1、水泥水化热 水泥在水化过程中要释放出一定的热量，而大体积混凝土结构断面较厚，表面系数相对较小，所以水泥发生的热量聚集在结构内部不易散失。这样混凝土内部的水化热无法及时散发出去，以至于越积越高，使内外温差增大。单位时间混凝土释放的水泥水化热，与混凝土单位体积中水泥用量和水泥品种有关，并随混凝土的龄期而增长。由于混凝土结构表面可以自然散热，实际上内部的最高温度，多数发生在浇筑后的最初3～5天。 2、外界气温变化 大体积混凝土在施工阶段，它的浇筑温度随着外界气温变化而变化。特别是气温骤降，会大大增加内外层混凝土温差，这对大体积混凝土是极为不利的。 温度应力是由于温差引起温度变形造成的;温差愈大，温度应力也愈大。同时，在高温条件下，大体积混凝土不易散热，混凝土内部的最高温度一般可达60～65℃，并且有较长的延续时间。因此，应采取温度控制措施，防止混凝土内外温差引起的温度应力。 3、混凝土的收缩 混凝土中约20℅的水分是水泥硬化所必须的，而约80℅的水分要蒸发。多余水分的蒸发会引起混凝土体积的收缩。混凝土收缩的主要原因是内部水蒸发引起混凝土收缩。如果混凝土收缩后，再处于水饱和状态，还可以恢复膨胀并几乎达到原有的体积。干湿交替会引起混凝土体积的交替变化，