冷轧板表面粗糙度对磷化膜微观形貌的影响 ·1 · 冷轧板表面粗糙度对磷化膜微观形貌的影响 李子涛 周世龙 张 武 张 军 刘永刚 （马鞍山钢铁股份有限公司汽车板推进处，安徽马鞍山 243000 ） 摘 要 使用粗糙度仪、扫描电镜等试验设备研究了不同粗糙度的冷轧 DC06 钢板的磷化膜微观形貌，结果表明： 随着Ra 值增加，钢板表面凹坑变大、变深，当 RPc 值增加，钢板表面凹坑变得更加密集；Ra、RPc 值增加均有利 于磷化成膜，即使 Ra 值较低，保持较高的 RPc 也能获得良好的磷化膜。 关键词 冷轧板，表面粗糙度，磷化膜，微观形貌 Influence of Surface Roughness of Cold-rolled Steel Sheet on Surface Morphology of Phosphate Coatings Li Zitao, Zhou Shilong, Zhang Wu, Zhang Jun, Liu Yonggang (Maanshan Iron Steel Co., Ltd., Auto Sheet Strategic Business Unit Cihu New District, Maanshan Anhui 243000, China) Abstract Roughness meter and SEM were used to study influence of surface roughness of cold-rolled steel sheet on surface morphology of phosphate coatings. The results showed that the more and deeper pits were observed with increasing Ra and RPc.Both the increased Ra and RPc were beneficial to develop phosphate coatings with fine and uniform crystalline grain.Even if the Ra value is low, high RPc can be also useful to obtain good phosphate coatings. Key words cold-rolled steel sheet, surface roughness, phosphate coatings, surface morphology 0 引言 磷化技术是一种重要的表面处理技术，广泛用于汽车涂装前处理行业，其主要作用是增加涂层与车身基 材的附着力以提高车身的耐蚀性，车身表面磷化膜的质量直接影响漆膜的耐蚀性和外观质量。从钢材本身来 说，对磷化过程存在较大影响的因素有表面粗糙度、表面残炭、表面氧化物等。 陈义庆等[1]的研究表明冷轧钢板表面粗糙度增加，磷化膜晶粒变得细小、均匀，膜重增大，并提出表面 [2]的研究认为 Ra 值较小， 粗糙度最好控制在 0 ．75～0 ．95 μm ，RPc 控制在 60～80 峰个数/cm 。郝晓东等 则 RPc 值较高，冷轧板在磷化过程中形核点较多，磷化膜更均匀致密。本工作利用粗糙度仪、扫描电镜等 试验设备，分析了不同表面粗糙度对冷轧钢板磷化膜微观形貌的影响。 1 试验部分 1.1 试验材料与方法 试验用材料为马钢与国内某钢厂的冷轧 DC06 产品。采用 HOMMEL T1000 型粗糙度仪测量裸板的粗糙 度。采用基恩士光学显微镜观察原始钢板表面形貌。采用扫描电镜观察磷化膜表面形貌。 李子涛