锆板制管和管弯头的开裂失效分析-上海焊接学会.pdfVIP

锆板制管和管弯头的开裂失效分析 杨惠谷 1 汪家军 2 顾福明 1 1 上海市特种设备监督检验技术研究院 2 上海贤达罗兰压力容器制造有限公司 摘要：某化工企业装置中，锆（Zr702 ）的板制管和管弯头，在生产过程和停车检修时发现 裂纹，并且已经贯穿内外。对出现裂纹的断口分析和能谱分析看，锆管的开裂是沿晶开裂。 开裂是由冷压成型中产生的残余应力，加上一定的温度、介质共同引起的，是由于力学因素 和焊接因素引起的。 Failure Analysis of a Zirconium Pipe and Elbow 1 2 3 Yang Huigu , Wang Jiajun , Gu Fuming 1 Shanghai Institute of Special Equipment Inspection and Technical Research 2 Shanghai Xianda Lorraine Pressure Vessel Manufacturing Co., Ltd. Abstract: Cracks were found to penetrate the wall thickness in a Zirconium (Zr702) pipe and elbow during operation, shut-down maintenance and repair in a chemical plant. Scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS) were used for the analysis of the fracture surface. The results showed us typical intergranular cracks. The failure was associated to residual stress after cold forming, temperature and medium. It had been concluded that the cracks were caused by combination of mechanical and welding factors. 0：前言： 锆是一种稀有金属，由于具有优良的耐蚀性能，高熔点、高强度，一直被 广泛应用于航空、航天、军工、原子能、医学等领域。锆及锆合金逐步进入化 工行业，但因其价格较高，仅在一些腐蚀条件较为苛刻的场合得到应用。如在 醋酸主装置中其物料腐蚀性很强，设备、管道、阀门及仪表等需采用价格昂贵 的特种合金材料。醋酸工程由于特殊性及介质腐蚀性，采用稀贵金属锆材和其 他特殊镍基合金材料制作设备和管道。锆容器在化工行业使用时间较短，国内 还没有相关的设计、制造规范和标准。 本文针对某化工企业装置中，锆（Zr702 ）的板制管和管弯头出现应力腐 蚀裂纹情况，采用扫描电镜和能谱对锆管裂纹断口分析，分析断口形貌的显微 组织和腐蚀产物的化学成分，结果表明，裂纹发生在基体金属—冷压制成型后， 该局部区域晶粒比较脆，从这锆板、管的裂纹看来，裂纹是从中间开裂的，它 们已经穿透到上、下表面，也即锆板的内、外表面。这也说明了开裂是由冷压 成型，应力没有消除，加上一定的温度、介质共同引起的，是由于力学因素和 焊接因素引起的。 1．锆（Zr702 ）的物理化学性质 锆在862℃以下具有密排六方晶体结构( α) ，高于这个温度时转变为体心 立方结构( β) 。少量的杂质尤其是氧，影响锆的转变温度。锆转变过程中；在冷 却时，会形成魏氏组织。锆是一种延展性金属，远没有钢致密。因它的熔点较 高(1845℃) ，所以在高温下化学性质比较活泼。金属锆是一种活泼性金属，相对 于标准氧电极，其25 ℃的氧化还原电位为-1.53V，