钴铬合金卡环纯钛卡环在钴铬金属冠上的固位力衰减及对冠表面磨损的研究.docVIP

钴铬合金卡环纯钛卡环在钴铬金属冠上的固位力衰减及对冠表面磨损的研究 　　 　　[摘要] 目的 探讨不同金属卡环作用于钴铬合金全冠时固位力变化规律及对冠表面磨损的影响。 方法 制作模拟天然牙外形的钴铬合金冠和钴铬合金卡环、纯钛卡环的标准试件，分两组进行1500次反复脱位和就位实验，比较两组钴铬合金全冠固位力衰减及对冠表面的磨损情况。 结果 电镜下可见纯钛卡环于钴铬合金全冠时的固位力、冠表面磨损情况均优于钴铬合金卡环。 结论 钴铬合金卡环、纯钛卡环在钴铬合金全冠上，均能提供足够的固位力，衰减剧烈程度：纯钛卡环组＜钴铬合金卡环组；对于冠表面的磨损程度：纯钛卡环组＜钴铬合金卡环组。 　　[关键词] 固位力衰减；磨损；纯钛卡环；钴铬合金冠；衰减曲线 　　[中图分类号] R783.1[文献标识码] A[文章编号] 1674-4721（2014）05（b）-0030-03 　　 　　Study of retentive force attenuation and its crown surface wear in the cobalt chromium metal crown of cobalt chromium alloy clasp and pure titanium clasp 　　GAO Xing-ping 　　Department of Stomatology,Rizhao People′s Hospital of Shandong Province,Rizhao 276826,China 　　[Abstract] Objective To investigate retention force changes′ law and the influence of crown surface wear when different metal clasp acting on cobalt chromium alloy crown. Methods Standard test piece of simulation of natural tooth shape of the cobalt chromium alloy crown and cobalt chromium alloy clasp, pure titanium clasp was made 　　and they were divided into two groups,then 1500 times of repeated dislocation and positioning experiment were conducted,the retentive force attenuation and crown surface wear in the cobalt chromium metal crown of the two groups were compared. Results The retentive force and crown surface wear in the cobalt chromium metal crown of the pure titanium clasp were better than those of cobalt chromium alloy clasp. Conclusion Cobalt chromium alloy clasp and pure titanium clasp in the cobalt chromium alloy crown can provide enough retention,decay severity degree:the pure titanium clasp 　　 　　表1 两组附着体经1500次摘戴固位力衰减情况的比较（x±s） 　　 　　 　　 　　 　　 　　3 讨论 　　烤瓷牙是先用合金制成金属基底（又叫内冠），再在其表面覆盖与天然牙相似的瓷粉，在真空条件下，借助高温的作用将陶瓷粉熔融并结合到经过特殊处理过的金属表面上而制作成的修复体。国内现在很多加工所宣称的钛合金烤瓷并不是真正的钛合金，是含钛4％～6％的镍基合金，对人体的潜在危害还是存在的。钛合金烤瓷牙的优点主要是生物相容性优于非贵金属，相当于75%的黄金合金，对镍离子敏感的人比较合适、比较耐久，可以避免牙龈出血和黑色牙龈现象的发生，能很好地恢复牙的形态和功能，且强度高、色泽好、耐磨损、耐腐蚀等，适合于绝大部分牙齿的修复。钴铬合金属于非贵金属烤瓷牙，而钛合金算是贵金属烤瓷牙，相对价格较高，钴铬合金最早是用于制作人工关节的，具有杰出的生物相容性，现已广泛应用于口腔修复领域。VEGO钴铬合金冠是