粗开孔型二次热处理精轧半钢轧辊生产.pdfVIP

粗开孔型二次热处理精轧半钢轧辊的研制 1/ 10 粗开孔型二次热处理精轧半钢轧辊的研制 黄进群 周国祥 戴中华 (常州凯达轧辊集团技术中心 ，江苏，常州) 摘 要：本文介绍了粗开孔型二次热处理精轧半钢轧辊生产研制情况。采用球化退火后，粗 开孔型，再进行二次热处理，使辊身表面和槽底得到相同的索氏体金相组织，从而取得了良 好的轧制效果；并将此经验成功移植到普通合金铸钢轧辊上。得出一个重要结论:半钢轧辊、 铸钢轧辊，热处理后的基体组织决定了其耐磨度和抗事故性能，耐磨度与轧辊硬度没有必然 联系。 关键词：孔型;二次热处理;半钢;精轧工作辊;铸钢轧辊 Study on Semi Steel Precision Roll after Crude Roll Pass and Second Heating Treatment HUANG Jin-qun, ZHOU Guo-xiang DAI Zhong-hua (Changzhou Kaida Roll Group CO.,LTD., Changzhou,Jiangsu 213155) Abstract: The study and production of the semi steel precision rolls after crude roll pass and second heating treatment are introduced in this paper. The sorbite structure can be obtained on the surface of roll body and in the groove bottom of roll after spheroidizing annealing and crude roll pass and second heating treatment. These can result in better rolling effects. The technology is also suitable for the production of ordinary alloy cast steels. An important conclusion can be drawn, i.e. for the semi steel rolls and the cast steel rolls, the wear resistance and anti-accidence performance depend on the matrix structure after the heating treatment, and the wear resistance has not positive connection with the roll hardness. Key words: roll pass; second heating treatment; semi steel; precision roll; cast steel roll 1、前言 随着国内大型型钢轧机数量的不断增加，型钢轧制的规格和品种也越来越多，轧辊材质 更新换代也越来越复杂，仅轧钢用精轧工作辊而言，也换了好几类材质。有使用半冷硬球墨 铸铁轧辊的，如武钢股份公司大型厂，在2007 年改造前，一直使用半冷硬球墨铸铁轧辊，采 取挂砂工艺铸造，辊身硬度为 3845HSD ，开槽后，组织粗大，不耐磨，换辊频繁；有些厂 家选用 CrMo、NiCrMo 无限冷硬球墨铸铁轧辊，辊身硬度为 5360HSD，采用冷型喷涂方式， 通过增加过冷度，使辊身石墨（G）、碳化物(K)、基体组织均得到细化，由于型钢轧辊孔型较 深，孔型底部激冷性很弱，硬度下降很快，传统的无限冷硬球墨铸铁轧辊，甚至无限冷硬珠 光体球墨铸铁轧辊，其耐磨性能也远不能满足轧制要求，如对比几家型钢厂，[16 成品机架 单孔一次过钢量仅在300 吨左右，且损孔频繁、辊耗大、轧机作业仍然低下。 我公