低掺量水性环氧树脂对高性能混凝土抗冻耐久性研究.pdfVIP

学兔兔 2012年第1期 混凝土与水泥制品 · 2012 No．1 1月 CHINA C0NCRETE AND CEMENT PRODUCTS January 低掺量水性环氧树脂对高性能混凝土 抗冻耐久性的研究 梁会忠，韩 飞，钱慧丽，王伟玲 (河北建材职业技术学院，秦皇岛066004) 摘 要：用快冻法研究了低掺量水性环氧树脂乳液对高性能混凝土抗冻耐久性的影响。结果表明，水性环氧树 脂乳液的加入可以显著提高混凝土的抗冻性。-3乳液掺量为5％时，采用Ⅳ型养护制度养护得到的高性能混凝土的 抗冻效果最好，在经历300次冻融循环后，相对动弹性模量可达94．1％；且水性环氧树脂能明显改善新拌混凝土的工 作性，易于施工。 关键词：低掺量水性环氧树脂；高性能混凝土；抗冻性 Abstract：The influences of low volume waterhome epoxy resin on freezing resistance durability of high performance concrete are investigated by accelerated freezing-thaw test．The results show that the addition of waterborne epoxy resin can obviously improve the freezing resistance of concrete．Th e freezing resistance effect is optimal when the dosage of wa- te~ome epoxy resin is 5％ and the curing system is the IV curing system．The relative dynamic modulus of elasticity is about 94．1％ by 300 times freezing-thaw cycle．and in addition．waterborne epoxy resin can improve the fluidity and work— ability of concrete obviously，which is easy for construction． Key words：Low volume waterborne epoxy resin；High perfm~nance concrete；Freezing resistance 中图分类号：TU528 文献标识码：A 文章编号：1000-4637(2012)01-09-04 0 前言 1 原材料与试验方法 混凝土耐久性是混凝土在设计使用寿命下保 1．1 原材料 持其所有功能的能力。混凝土是最大宗的建筑材 (1)水性环氧树脂：上海某公司生产的水性环 料，提高混凝土耐久性具有非常重要的理论意义和 氧树脂H213A和水性环氧固化剂H213B，使用配比 经济价值。在严寒季节，混凝土建筑结构遭受冻融 为质量比，水性环氧树脂H213A：水性环氧固化剂 破坏，每年需花费巨资加以修复口1。因此，混凝土的 H213B=l：1．4，水性环氧固化剂组分中固含量为 冻融破坏是我国建筑物老化病害的主要问题之一， 50％，其余为水；(2)水泥：河北某公司生产的42．5 严重影响了建筑物的长期使用和安全运行，为使这 级普通硅酸盐水泥；(3)细集料：河北正定产河砂， 些工程继续发挥作用和效益，需要很大的代价来维 试验测得为中砂；(4)粗集料：级配良好的碎石，粒 修和重建，这已成为混凝土耐久性方面的主要问题