再生骨料级配对再生混凝土多孔砖干燥收缩影响.pdf

学兔兔 全国中文核心期刊 新勉 盔巍 嘲 再生骨料级配对再生混凝土 多孔砖干燥收缩的影响 胡利，梁建国，杨伟军，李鹏飞 (长沙理工大学 土木与建筑学院，湖南 长沙 4101 14) 摘要：对不同碎砖和细骨料含量的再生混凝土多孔砖进行干燥收缩率试验研究。结果表明，再生混凝土多孔砖干燥收缩率随碎 砖骨料掺量的增加而增大，随着细骨料掺量的增加而减小。 关键词：再生混凝土；多孔砖；配合比；骨料级配；干燥收缩 中图分类号：TU522．1 文献标识码：A 文章编号：1001—702X(2011)04—0024—04 Effect of aggregate gradation on drying shrinkage of recycled concrete perforated brick HU Li，LIANG Jianguo，YANG We~un，LI Pen~ei (School of Civil Engineering＆ Architecture，Changsha University of Science＆Technology，Changsha 4101 14，Hunan，China) Abstract：The drying shrinkage of recycled concrete perforated brick with different content of broken bricks and recycled fine aggregate was tested．The test results show that the drying shrinkage of recycled concrete perforated brick increases with the rais— ing of broken bricks content，and decreases with the raising of recycled fine aggregate content． Key words：recycled concrete：perforated brick；mixture ratio：aggregate gradation：drying shrinkage 使得5 mm以下的再生骨料得以全部利用。 0 引 言 本研究将对7种不同配合比的再生混凝土多孔砖进行干 随着城镇化建设步伐的加快，我国每年因城市改造拆除 燥收缩试验，重点研究再生骨料级配对再生混凝土多孔砖干 的废旧建筑将产生大量的建筑垃圾，依照传统的方式占地堆 燥收缩性能的影响。 积处理，不仅浪费耕地，而且污染环境。据报道，长沙市2003 1 再生混凝土多孔砖用骨料性能及 年房屋拆迁面积42．9万m ，按每平方米产生1．0 1．5 t建筑 配合比设计 垃圾计算，加上新建房屋产生的建筑垃圾，总量超过100万 t，处理的费用更是高达124．35元h。如何解决建筑垃圾的回 再生骨料采用长沙市区废旧建筑拆下来的混凝土块和砖 收和利用，对我国城镇化建设有着重要的意义。 块，经砖厂细碎机破碎和人工筛分工艺后得到粒径0—5 mm 将建筑垃圾经过专业生产工艺处理后得到的再生骨料具 的细骨料和粒径5