核电用钛钢复合板制备技术研究核电用钛钢复合板制备技术研究.pdf

Material Sciences 材料科学, 2015, 5(6), 235-241 Published Online November 2015 in Hans. /journal/ms /10.12677/ms.2015.56032 Manufacture Technology of Ti-CS Clad Plate for Nuclear Station Jun Song, Hui Zhao, Pingcang Li Xi’an Tianli Metal Composite Material Co. Ltd., Xi’an Shaanxi th th th Received: Nov. 5 , 2015; accepted: Nov. 24 , 2015; published: Nov. 27 , 2015 Copyright © 2015 by authors and Hans Publishers Inc. This work is licensed under the Creative Commons Attribution International License (CC BY). /licenses/by/4.0/ Abstract In this paper, computer simulation was employed to optimize the manufacturing process of the Ti-CS clad plate. Then the clad plate was inspected and tested with OP, SEM and mechanical prop- erties. The test results show that, the clad plate interface is wavy. And no departure, melted block or other defect was inspected in the interface. Shearing test results showed that the bonding strength is more than 200 MPa. It meets the requirements of the specification. Moreover, after bending, the sample also showed good properties. Keywords Nuclear Station, Ti-CS Clad Plate, Explosive Bonding 核电用钛钢复合板制备技术研究 宋 军，赵 惠，李平仓 西安天力金属复合材料有限公司，陕西 西安 收稿日期：2015年11月5 日；录用日期：2015年11月24 日；发布日期：2015年11月27 日 摘 要 本文采用计算机模拟法优化爆炸焊接工艺参数，然后制备出核电用复合板。从金相检验、SEM和力学性 文章引用: 宋军, 赵惠, 李平仓. 核电用钛钢复合板制备技术研究[J]. 材料科学, 2015, 5(6): 235-241. /10.12677/ms.2015.56032 宋军 等 能检验结果来看，复合材的界面均匀，呈现爆炸焊接所特有的波状界面，且界面处无分层、熔化等缺陷。 剪切试验结果说明复合板结合强度高于200 MPa，弯曲满足核电领域使用要求。 关键词 核电，钛复合材，爆炸焊接 1. 前言 随着经济的蓬勃发展，能源紧缺越来越突出。核电是和平利用核能的重要形式。自从我国首座自主 设计建造的秦山核电站于1991 年 12 月15 日实现首次并网发电以来，截至2014 年5 月，我国大陆已建