Evaluation and selection of hard coatings for micro milling of hardened tool steel英文电子书.pdfVIP

ARTICLE IN PRESS International Journal of Machine Tools Manufacture 48 (2008) 1578– 1584 Contents lists available at ScienceDirect International Journal of Machine Tools Manufacture journal homepage: /locate/ijmactool Evaluation and selection of hard coatings for micro milling of hardened tool steel A. Aramcharoen a,, P.T. Mativenga a, S. Yang b, K.E. Cooke b, D.G. Teer b a Manufacturing and Laser Processing, School of Mechanical, Aerospace and Civil Engineering, The University of Manchester, Manchester M60 1QD, UK b Teer Coatings Ltd., UK a r t i c l e i n f o a b s t r a c t Article history: In conventional or macroscale milling, appropriate physical vapour deposition (PVD) coatings can be Received 14 March 2008 used to improve machining performance, promote the use of higher cutting speeds and facilitate dry Received in revised form machining or the use of minimum quantity lubrication (MQL). When micro tools (1–999 mm in 17 May 2008 diameter) are used in milling, the undeformed chip thickness is usually very small and comparable to Accepted 27 May 2008 the cutting edge radius. This condition determines the effective rake angle and hence plays a significant Available online 10 June 2008 role in the mechanics of micro machining. The differences between macro and microscale machining Keywords: influence process factors such as cutting interfac