磷铝酸盐水泥修复硅酸盐水泥混凝土的性能研究.pdfVIP

磷铝酸盐水泥修复硅酸盐水泥混凝土的性能研究 李虹燕 丁铸 邢锋 （深圳大学土木工程学院；深圳市土木工程耐久性重点实验室 深圳 518060） 摘要 本文以新型磷铝酸盐水泥(PALC)为修补材料，研究了它与传统硅酸盐水泥(PC)之间的修复性能，粘 结料为磷铝酸盐水泥砂浆和硅酸盐水泥砂浆。还利用 RCM 方法通过对比磷铝酸盐混凝土和硅酸盐混凝土 的快速氯离子渗透性试验，定量说明氯离子在两种混凝土中的渗透作用。结果表明：磷铝酸盐水泥砂浆与 硅酸盐水泥砂浆的粘结强度比硅酸盐水泥砂浆与硅酸盐水泥砂浆高，而且修补材料本身早期强度高，后期 强度持续发展不倒缩；磷铝酸盐的混凝土的抗氯离子渗透性明显比硅酸盐的混凝土好。 关键字 磷铝酸盐水泥；高性能；氯离子渗透；混凝土修补 Property of Phosphoaluminate Cement Repaired Portland Cement Concrete LI Hongyan, DING Zhu, XING Feng (School of Civil Engineering, Shenzhen University; The Shenzhen Key lab on Durability of Civil Engineering, Shenzhen 518060) Abstract Property of Portland cement (PC) concrete repaired with Potland cement mortar and phosphoaluminate cement (PALC) mortar were investigated. Rapid chloride ion penatration test of PALC concrete and Portland cement concrete were also carried out. The penatration effect of chloride ion in the two types conccrete were elucidated. The results showed that, the bonding strength between PALC mortar repaired PC sample is better than that of PC moratr repaired PC sample. PALC has high strength in the early age and its long strength will continuously develop. The chloride ion penatration resistance of PALC concrete is also higher than that of PC concrete. Keywords phosphoaluminate cement, high performance, chloride ion penatration, concrete repair 0 前言 题，引起了社会广泛关注。当今世界各国都在研究 和发展专用水泥及特种水泥。水泥已从单一的含硅 水泥是世界上用量最大的重要建筑材料，2005 酸盐矿物的品种发展到各种化学成分、矿物组成、 年我国水泥年产量 10.64 亿吨，占世界水泥产量的 性能与应用范围不同的品种。 三分之一[1] 。我国正处在快速建设与发展期，对水 混凝土建筑物和构件在使用期间受腐蚀而产 泥性能及工程质量的要求越来越高，由于传统硅酸 生破损的现象屡见不鲜。破坏的建筑物的重建是耗 盐水泥固有的性能和特点，决定了它不能满足一