混凝土结构钢筋腐蚀的影响因素与防护.docxVIP

郑州大学土木工程学院硕士研究生课程论文课程名称《工程结构耐久性》学时36学分2 姓名主讲教师指导教师培养类型：□科学学位?专业学位□工程硕士□高校教师年级 12级学号供职单位无联系电话Email 提交日期2013.5.29 混凝土结构钢筋腐蚀的影响因素及防护姓名：郑萌立学号：201222212462 郑州大学土木工程学院摘要：钢筋混凝土结构从出现到21世纪，经历了比较久的发展时期，并且依旧占据着建筑结构中最重要的一部分。然而，近年来的工程实际情况表明，在役钢筋混凝土结构因为耐久性问题而引起破坏的现象越来越严重，因此，有必要对钢筋锈蚀对混凝土结构耐久性的影响做研究。尤其是混凝土中影响钢筋锈蚀的因素与针对这些因素所采取的措施。关键词：混凝土结构；耐久性；钢筋锈蚀；预防措施Factors Influencing The Corrosion of Steel In Concrete And Its ProtectionName：ZHENG Meng-li ID：201222212462 School of Civil Engineering of Zhengzhou UniversityAbstract：From being create to twenty-first century，Reinforced concrete structure experienced a period of development for a long time, and still plays the most important part of the building structure. However, the actual situation of the project shows that in recent years, the damage caused by durability problems in existing reinforced concrete structure is more and more serious, which is leaded by the orrosion of steel bar give a large part. Therefore, it is necessary to do research on the influence of reinforcement corrosion on the durability of concrete structures. Especially the influence factors of steel corrosion in concrete and the measures taken in response to these factors.Keywords：reinforced concrete structure； durability； corrosion； prevention measures0 引言最开始人们认为，钢筋混凝土结构很好地结合了钢筋与混凝土材料的优点，可模性好、可塑性强、整体性好、耐久性好、后期维护费用较低以及易于就地取材等诸多优点使得当今世界上的建筑大多选择采用钢筋混凝土结构。但随着时间的推后与累积，钢筋混凝土结构远远没有人们当初想象的那样耐久，其良好性能会在使用期内由于诸多因素的影响而逐渐退化从而引起世界上对耐久性问题的关注。特别是由于混凝土中钢筋的腐蚀引起的混凝土可靠性的降低[1]。随着腐蚀的加剧将导致混凝土保护层开裂、钢筋与混凝土间粘结力破坏、钢筋受力截面减小、结构强度降低等一系列不良后果。据统计全世界每年因混凝土结构耐久性问题造成的社会经济损失十分巨大。美国目前整个混凝土工程的价值约为60000亿美元，每年用于维修或重建的费用竟高达3000亿美元；英国建筑工业年成交额为500亿英磅，而因腐蚀损坏，钢筋混凝土结构的年维修费用高达515亿英磅，已成为英国的一个沉重的财政负担。我国的混凝土结构耐久性问题同样不容忽视，20世纪70年代末，我国开始兴建大量立交桥，20世纪90年代时发现混凝土保护层剥落，钢筋锈蚀等严重损坏现象，急需进行维修、加固，甚至重建，造成社会财富的巨大浪费[2]。我国由于社会、经济以及历史原因，对于混凝土耐久性的关注与研究起步较晚，在建设领域还贯穿着“重建设，轻耐久”的思想。在美国，“立足前期措施、着眼长远效益”，美国经过正反两个方面的经验教训所得出的可贵结论已成为美国建设领域的重要思想。美国正在强行实施基建工程管理中的“全寿命经济分析法”(LCCA) ，其基本思想是，在设计施工阶段，不论是事先采取防护措施还是以后“坏了再