添加La对PrFeB薄带的结构与磁性能影响.pdfVIP

Material Sciences 材料科学, 2017, 7(9), 745-751 Published Online December 2017 in Hans. /journal/ms /10.12677/ms.2017.79097 The Effects of La-Doping on Structure and Magnetic Properties of PrFeB Ribbons Xiaoyu Yao, Pengcheng Yang, Qingrong Yao* School of Materials Science and Engineering, Guilin University of Electronic Technology, Guilin Guangxi st rd th Received: Nov. 21 , 2017; accepted: Dec. 3 , 2017; published: Dec. 11 , 2017 Abstract (Pr La ) Fe B (x = 0.0 - 0.25) alloy ribbons were prepared by melt quenching and heat treat- 1−x x 2 14 ment, and its crystal structure was tetragonal structure with P42/mnm space group. And the lat- tice parameters increase with an increase of La concentration. The magnetic properties and mi- crostructure of the ribbons with annealed different time and temperature were studied by me- thods of VSM and SEM. The results show that the undoped La thin strip has the highest remanence, which is 1.05 T. Moreover, the (Pr La ) Fe B alloy at the rapid quenching speed of 25m/s and 0.9 0.1 2 14 the temperature at 873 K for 5 min has a best comprehensive performance. Excessive crystalliza- tion temperature and prolonged crystallization time will affect the magnetic properties of the ribbons. Keywords Melt-Spun Ribbon, Magnetic Property, Microstructure 添加La对PrFeB薄带的结构与磁性能影响 姚小玉，杨鹏程，姚青荣* 桂林电子科技大学材料科学与工程学院，广西 桂林 收稿日期：2017年11月21 日；录用日期：2017年12月3 日；发布日期：2017年12月11 日 摘 要 采用熔体快淬和热处理工艺制备了(Pr La ) Fe B (x = 0.0~0.25)合金薄带，其晶体结构为四方结构 1−x x 2 14 *通讯作者。 文章引用: