Research on the performance of waterproof and moisture permeable PU film laminated fabrics Abstract：With polyester fabric,hot melt rubber TPU and PU film of high moisture permeable as basic material, the waterproof and moisture permeable composite fabric was prepared by laminated composite method. The tensile,pendant,air permeable,waterproof and moisture permeable performance of polyester fabric, PU film and composite fabric were tested. The effect of different amount of TPU,composite temperature and composite pressure on the performance of composite fabric were discussed. The results showed that the tensile strength of composite fabric was improved at certain degree after the polyester and PU film were composited,but the pendant performance of the composite fabric was worse than that of polyester fabric,the waterproof effect of composite fabric was better than that of polyester fabric obviously,while the air and moisture permeable performance of the composite fabric were worse than that of PU film. When the amount of TPU with 22 g/m2,composite pressure of 5 MPa,composite temperature of 80 °C,the composite effect of the composite fabric is the best. Along with the rapid development of science and technology, especially the advanced science and technology development, sex for spinning weaving product can carry out more to the higher, more to the more requirements.The appearance and development of waterproof and moisture permeable fabric is the result of modern science and technology progress, is also the fabric design aspects of a breakthrough.Waterproof and moisture permeable fabric is textile industry for many years set to waterproof and moisture permeable, windproof, warm in the integration of high-tech products, it can arrive the rain of the snow and cold wind attack, can let person body khan gas and line up, keep dry cool and warm warm, is a straight in many years, people trying to develop a kind of similar to natural leather material.PU membrane is a thin layer