非接触式无损检测木材干燥应力的方法 （安磊 高建民 ） （ 北京林业大学 北京 100083 ） 摘要 木材干燥应力是干燥过程中产生干燥缺陷的主要因素。文章根据数字散斑相关方法（DSCM）检测应力的原理设计出了一种非接触式无损检测木材干燥过程中应变的方法，用木材干燥表面测点位移的变化速率即应变速率来表示木材干燥过程中应力状态，初步提出了建立木材干燥应力评价体系的设想。研究结果表明：木材表面测点位移变化量与时间存在着对数关系，与含水率变化量则呈线性关系。 关键词：木材干燥，干燥应力，无损检测。 中文分类号： 文献标识码： 文章编号： The method of non-destructive detecting wood drying stress AnLei GaoJianmin （ Beijing Forestry University,Beijing,100083 ） Abstract The drying stress is the main reason that causes the drying defects. It is designed the method of non-destructive detecting wood drying stress, according the digital speckle correlation method (DSCM), it is the first time to mention how to build up a judging system by straining velocity which is represented the drying stress .The results of this study show that: the displacement of the testing point has a logarithm relationship with the time of drying; however, it has a linear relationship with the changing of moisture content. Key words Wood drying，Drying stress，Non-destructive 木材干燥应力是产生木材干燥缺陷的主要因素，因此成为研究和制定木材干燥工艺基准的一个主要参数和依据。自20世纪三十年代以来，国内外许多学者致力于这一课题的研究，使得木材干燥应力的理论和方法不断完善和发展。西尾茂于20世纪七十年代初提出用瓦弯法测定木材干燥应力[1] [2]，Tang根据木材收缩各向异性的原理，指出了弦高法(瓦弯法)测定 ———————————————————— 作者介绍 安磊 北京林业大学材料科学与技术学院硕士研究生 木材干燥应力的数学模型[3]。1982年周宝华按照前苏联学者乌戈列夫的试验方法，根据在弹性范围内木材的应力与应变成正比的原理，初步探索出木材在窑干过程中内应力发展和变化的规律[]。，[5]。 木材干燥是一个复杂而又多变的过程，虽然许多学者在自己研究的领域取得了一定的成绩，但始终没有找到一个令人满意的应力应变测试方法，也没有形成一个科学的木材干燥应力检测的研究思路。 传统的测量方法认为木材干燥过程中应力的变化情况和应变的变化情况是同步的，因此以往的木材干燥应力的检测方法都是基于木材干燥应变最大时应力也最大的论断而得出的，传统的测量方法认为木材干燥过程中应力的变化情况和应变的变化情况是同步的，但本次研究表明应变最大的时刻却不一定是应力最大的时刻，因此木材干燥过程中的变形将会比干燥应力有所延迟，这主要是因为木材是弹塑性材料，变形是应力长期作用的结果。为了更好的 研究和探索木材在干燥过程中的木材干缩和干燥应力之间的关系，本实验基于数字散斑相关方法的一个变形的实验原理，着重研究木材干燥过程中木材厚度方向上干缩的变化， 在试 材厚度方向上来考虑几个已知点的距离，通过距离的变化来近似的考察这些点的位移变化，从而分析木材干燥过程中应力的变化。 1．实验材料与方法 1.1实验材料 楸木（Liriodendron chinense）板材，取自北京强力家具厂，试材大小是200mm×150mm×54mm的径切板，并从中部锯取10mm厚的薄片用于测量试材的初含水率。初含水率按阔叶树锯材干燥基准表要求进行操作[6]，在102℃下烘到绝干，得到初含水率约为34.5%。两端采用蓝星新材料无锡树脂厂产的环氧树脂及上海树脂厂有限公司生产的固化剂封端。 1.2实验设备 电热恒温鼓风干燥箱，可以设定需要的温度、是否通风等；非接触式显微测试仪采用Dyna