10.2烧结过程及机理.pptVIP

第十章 烧结过程——10.2烧结过程及机理 第十章 烧结过程——10.2烧结过程及机理 10.2 Sintering Process and Mechanisms Sintering process Drive force of sintering Sintering mechinsms 第十章 烧结过程——10.2烧结过程及机理 Sintering process 1.1 Impact of temperature on sintering body  l－Conductivity ；2－Strength；3－Density Conductivity (Ω-1·cm-3) Temperature (°C) Density (g/cm2) Cu powders Strength (MPa) 第十章 烧结过程——10.2烧结过程及机理 Temperature increases, conductivity, density and strength increase. Conductivity and strength increase before density increases It is difficult to get fully dense samples by normal sintering 第十章 烧结过程——10.2烧结过程及机理 2. Sintering model 第十章 烧结过程——10.2烧结过程及机理 Three stages of sintering Preliminary： Re-arrange of powders，bonding among powders，deform of void Middle： Start to mass transfer，deform of powders Late： Growth of some powders and disappear of some powders 第十章 烧结过程——10.2烧结过程及机理 2 Drive force Decrease of surface energy (Surface tension) Sintering is a irreversible process. 第十章 烧结过程——10.2烧结过程及机理 Because of surface tension, P P0： For spherical surface: （1） For nonspherical surface （2） 第十章 烧结过程——10.2烧结过程及机理 P1 P1 P2 P0 P1P0P2 Gas or liquid phase migrate Flow and Diffusion 第十章 烧结过程——10.2烧结过程及机理 3. Mechanisms 1. Adhesive attraction of powders 2. Mass transfer 第十章 烧结过程——10.2烧结过程及机理 1. Adhesive attraction of powders Due to surface tension Two glass fibers Powders 第十章 烧结过程——10.2烧结过程及机理 Adhesive attraction of two particles with liquid film (a) (b) ρ 第十章 烧结过程——10.2烧结过程及机理 2 Mass transfer Flow Diffusion Evaporation-condensing (Gas phase) Dissolve-precipitation (Liquid phase) 第十章 烧结过程——10.2烧结过程及机理 1．Flow Mass flow Drive by applied force Type: Viscous flow (Newton fluid) Plastic flow (Bingham fluid) ：