毕业设计（论文）-基于高导热透明陶瓷的激光二极管LD器件封装与光电特性研究精选.docxVIP

毕业论文 院系名称 机械工程系 目录中文摘要:1英文摘要:21文献综述31.1LED与LD简介31.2LED封装技术与产生白光原理61.3激光二极管LD的研究进展71.4白光LED荧光材料111.5LD荧光转换材料与透明陶瓷材料121.6YAG 透明陶瓷概论161.7Y2O3-Al2O3的二元系统相图181.8本课题研究的目的及意义192实验部分212.1实验材料212.2实验器材222.3研究过程233结果与讨论243.1YAG：Ce的光致发光性能243.2YAG：Ce的吸收性能253.3LD发射光谱与光电参数273.4白光LD器件的光学性能283.5白光LD器件的色度333.6白光LD器件的电学性能354研究结论与展望364.1主要工作364.2有待进一步开展的工作37致谢38[参考文献]39基于高导热透明陶瓷的激光二极管LD器件封装与光电特性研究摘要:激光二极管(LD)是继发光二极管（LED）之后的下一代半导体照明与显示器件。它具有效率高、体积小、质量轻、代价低、连续输出波长范围宽和光脉冲输出高等优点。但是因为它方向性比较强，所以其照射出的光是一个亮度极高的光斑。为了探索LD未来的应用技术。本文采用具有高导热的YAG：Ce透明陶瓷作为白光配光材料，研究了利用450nm蓝色激光激发YAG：Ce黄色透明陶瓷产生白光的可能。研究结果表明：在发光性能方面随着Ce浓度的提高，白光区域占光的总强度的百分比逐步提高；在显示指数方面，随着Ce浓度的降低，显色指数在逐渐升高；在色品图方面，随着Ce浓度的上升，色坐标在逐步的向黄色的光方向移动，其中0.1 at.%的Ce:YAG透明陶瓷最接近理想白点；在透射率方面，随着掺杂Ce浓度的提高，透射率在逐步下降；在光致发光光谱(PL)方面，Ce:YAG陶瓷中Ce3+的最佳替代浓度为x =0.3~0.5 at.％；在光效方面，随着Ce浓度的降低，光效在逐步的升高。关键词：Ce:YAG；透明陶瓷；激光二极管；光学性能；电学性能；Abstract: The laser diode (LD) is the next generation of semiconductor lighting and display devices following the light emitting diode (LED). Laser diodes have the advantages of high efficiency, small size, and light weight small size and light weight, low price, continuous output wavelength range and high optical pulse output. But because of its relatively strong direction, so the light is a light of a very high brightness spot. In order to explore the future application of LD technology. In this paper, YAG: Ce transparent ceramics with high thermal conductivity as white light distribution material was used to study the possibility of generating white light by stimulating YAG: Ce yellow transparent ceramics with 450nm blue laser. Research indicates:With the increase of Ce concentration, the white light area gradually increases the percentage of the total intensity of light; In the display index, with the decrease of Ce concentration, the color rendering index gradually increased; In the aspect of chromaticity diagram, as the increase of Ce concentration, the color coordinates move in the direction of yellow light gradually, of which 0.1 at