真空热处理对2024-T6铝合金无电镀镍磷钻石石墨烯复合镀层-YOKE.PDFVIP

真空熱處理對2024-T6 鋁合金無電鍍鎳磷/鑽石/石墨烯複合鍍層之導電性、磨耗與 腐蝕的影響研究 Effect of Vacuum Annealing Treatment on the Conductivity, Wear and Corrosion Properties of Electroless Ni-P/Diamond /Graphene Composite Coating on 2024-T6 Alloy 1 2 3* 李正國 周趙遠鳳 鄧吉倫 1 2,3* 健行科技大學機械工程系 健行科技大學電子工程系 Cheng-Kuo Lee1 Yuan-Fong Chau2 Chi-Lun Teng3* 1Department of Mechanical Engineering, 2,3*Department of Electronic Engineering Chien Hsin University of Science and Technology 摘 要 wear-corrosion resistance of the alloy in 3.5 wt% 本研究在經適當陽極處理後的 2024-T6 鋁合金 NaCl solution. The electroless 基材表面以無電鍍法鍍析出鎳磷/鑽石/石墨烯 Ni-P/diamond/graphene plating solution was 複合鍍層，探討添加不同大小鑽石粒子(6-12 μm prepared by adding different size diamond (6-12 與 0.2 μm)與經由真空退火熱處理後的Ni-P 複 μm and 0.2 μm) and nano-graphene into the 合鍍膜的表面結構、導電性、耐磨耗腐蝕與耐 electroless Ni-P plating solution to obtain different 腐蝕性的影響效應 。研究結果顯示2024-T6 鋁 Ni-P/diamond, Ni-P/graphene and 合金經由陽極處理後可成功地析鍍上 Ni-P/daimond/graphene composite coatings for N-P/diamond/graphene 複合鍍層，更能增加表面 comparison. Experimental results indicated that 硬度 ，也能提供2024-T6 鋁合金基材的腐蝕與 the electroless N-P/diamond/graphene composite 磨耗腐蝕保護性 。石墨烯的添加可降低電阻率 coating could be successfully electroless deposited 與提供潤滑性，使 Ni-P/diamond/graphene 有最 upon suitable anodized 2024-T6 aluminum alloy 佳的耐磨耗腐蝕性，尤其添加較細小的鑽石粒 substrate. The composite coating had a